The article presents the application of the acoustic emission (AE) technique for detecting crack initiation and examining the crack growth process in steel used in engineering structures. The tests were carried out on 40CrMo steel specimens with a single edge notch in bending (SENB). In the tests crack opening displacement, force parameter, and potential drop signal were measured. The fracture mechanism under loading was classified as brittle. Accurate AE investigations of the cracking process and SEM observations of the fracture surfaces helped to determine that the cracking process is a more complex phenomenon than the commonly understood brittle fracture. The AE signals showed that the frequency range in the initial stage of crack development and in the further crack growth stages vary. Based on the analysis of parameters and frequencies of AE signals, it was found that the process of apparently brittle fracture begins and ends according to the mechanisms characteristic of ductile crack growth. The work focuses on the comparison of selected parameters of AE signals recorded in the pre-initiation phase and during the growth of brittle fracture cracking.

Durability, safety, and usability are the three foundations of structural reliability, vital in the economic and social context. As the locating and tracking of potential damage and evaluating its impact on the condition of the structure are part of service life assessment, relevant methods should be developed that would detect the onset of the deterioration process and enable the monitoring of its progress within the entire volume of the structure, not only in the areas selected in a subjective way. The acoustic emission (AE) method relying on the analysis of active destructive processes can be the best choice. This article reports the results of the application of the AE method for identifying active destructive processes and tracking their development during the routine operation of various types of structures.

This article presents a concise review of modern non-destructive testing (NDT) methods that allow the detection, tracking, and measurement of cracks in reinforced concrete structures. Over the past decades, the range of solutions available on the market has increased. This provides excellent opportunities when choosing and designing systems for diagnosing and continuously monitoring structures. Cracking affects the mechanical properties, durability, and serviceability of a structure or its elements. Therefore, there is a need to develop methods that would allow the determination of the moment of a destructive process’s formation, i.e., a crack’s appearance. At the same time, it is crucial to be able to track the development of cracks for the entire structure, not just selected locations. This work also presents the concept of combining selected NDT methods and creating a system for the continuous monitoring of structural integrity and predicting changes in the durability of existing and future buildings.

The commercialization of modular timber products as cost-effective and lightweight components has resulted in innovative engineering products, e.g., glued laminated timber, laminated veneer lumber, I-beams, cross-laminated timber and solid timber joined with wedge joints. With the passage of time, timber structures can deteriorate, or new structural elements are required to increase the stiffness or load-bearing capacity in newly built structures, e.g., lintels over large-scale glazing or garages, or to reduce cross-sectional dimensions or save costly timber material while still achieving low weight. It is in such cases that repair or correct reinforcement is required. In this experimental and numerical study, the static performance of flexural timber beams reinforced with prestressed basalt BFRP, glass GFRP and hybrid glass–basalt fiber bars is shown. The experimental tests resulted in an increase in the load-carrying capacity of BFRP (44%), GFRP (33%) and hybrid bars (43%) and an increase in the stiffness of BFRP (28%), GFRP (24%) and hybrid bars (25%). In addition to this, glued laminated timber beams reinforced with prestressed basalt rods subjected to biological degradation, 7 years of weathering and prolonged exposure to various environmental conditions were examined, and an increase in the load-bearing capacity of 27% and an increase in stiffness of 28% were obtained. In addition, full-size laminated timber beams reinforced with prestressed basalt bars were investigated in the field as an exploratory test under fire conditions at elevated temperatures, and the effect of the physical–mechanical properties during the fire was examined via an analysis of these properties after the fire. In addition, a satisfactory correlation of the numerical simulations with the experimental studies was obtained. The differences were between 1.1% and 5.5%. The concordance was due to the fact that, in this study, the Young, Poisson and shear moduli were determined for all quality classes of sawn timber. Only a significant difference resulted in the numerical analysis for the beams exposed to fire under fire conditions. The experimental, theoretical and numerical analyses in this research were exploratory and will be expanded as directions for future research.