A notch-induced high-speed splitting method was developed for high-quality cropping of metal bars using a new type of electric-pneumatic counter hammer. Theoretical equations and FE models were established to reveal the crack initiation and fracture mode. Comparative tests were conducted for notched and unnotched bars of four types of steels, i.e., AISI 1020, 1045, 52100, and 304, and the section quality and microfracture mechanism were further investigated. The results show that damage initiates at the bilateral notch tips with peak equivalent plastic strain, and propagates through the plane induced by the notch tip; the stress triaxiality varies as a quasi-sine curve, revealing that the material is subjected to pure shearing at the notch tip, and under compression at the adjacent region. High precision chamfered billets were obtained with roundness errors of 1.1–2.8%, bending deflections of 0.5–1.5mm, and angles of inclination of 0.7°–3.4°. Additionally, the notch effectively reduced the maximum impact force by 21.6–23.9%, splitting displacement by 7.6–18.6%, and impact energy by 27.8–39.1%. The crack initiation zone displayed quasi-parabolic shallow dimples due to shear stress, and the pinning effect was larger in AISI 52100 and 1045 steel; the final rupture zone was characterized by less elongated and quasi-equiaxial deeper dimples due to the combination of shear and normal stress.

A laser-assisted high-speed shearing (LAHSS) method has been proposed for metal bars, which prefabricates equally spaced fracture-start kerfs by Nd:Yag laser to make stress concentration, and applies a high-speed load to complete fracture separation. Comparative tests were conducted for Q235, 40Cr, and 304 steel bars, and the effects of fracture-start kerfs and axial clearance were investigated on the fracture section. Moreover, the fracture behavior was demonstrated by numerical simulation, and the micro-fracture mechanism was revealed by fractographic analysis. The numerical simulation results show that the material damage concentrates along with the kerf tips with peak equivalent plastic strain, and the corresponding stress triaxiality drops to almost zero at the kerf tip, which reveals that the material is subjected to pure shearing at kerf tip; the Max. loading force is reduced by 15.2%–29.6%, and the impact energy is decreased by 29.8%–46.9% for the three types of bar material. The experimental results showed that the fracture-start kerfs effectively inhibited the plastic deformation stage, and higher precision blanks were obtained in the LAHSS test: roundness error improved from 2.7%–10.9% to 1.1%–2.6%, Max. bending deflection decreased from 1.3–3.4 mm to 0.4–1.0 mm, and flatness error dropped from 0.9–3.3 mm to 0.3–0.7 mm. The fractographic analysis reveals that the crack initiation is related to alternative V-shape micro-notches at the laser-affected zone; the predominant fracture mechanism involves mode II microvoid coalescence at the main fracture plane; smaller and less elongated dimples were formed in 40Cr steels due to higher number density of grains and pinning effect of second-phase particles compared to Q235 and 304 steel bars.