Natural fiber reinforced polymer-based composites have been growing into a type of green composites. The properties of natural fiber reinforced polymer-based composites are closely related to the structure of natural fibers. Bagasse fiber (BF) is one of the most used natural fibers for preparing natural fiber reinforced polymer-based composites. However, few examples of previous research touch on the quantitatively characterization of structure of BF and its effect on the properties of BF reinforced polymer-based composites. In this work, four kinds of BF including untreated BF (UBF), alkali treated BF (ABF), BF modified by silane coupling agent (SBF), and BF modified combining alkali treatment with silane coupling agent (ASBF) were prepared and melting blended with polylactic acid (PLA) to prepare PLA/BF composites. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), thermogravimetry (TGA) and mechanical properties testing were used to characterize and analyze the structure and properties of modified BF and its reinforced PLA-based composites. Results showed that the used methods changed the structure of BF and their bonding modes. The surface energies of UBF, ABF, SBF, and ASBF were 19.8 mJ/m², 34.7 mJ/m², 12.3 mJ/m², and 21.6 mJ/m², respectively. The O/C ratios of UBF, ABF, SBF and, ASBF are 0.48, 0.53, 0.47, and 0.51. Due to the synergistic effect of alkali treatment and silane coupling agent modification on the surface chemical properties, the content of silicon elements on the surface of ASBF (4.15%) was higher than that of ASBF (2.38%). However, due to the destroying of alkali treatment on the microstructure of BF, the alkali treatment had no prominently synergetic effect with coupling agent modification on the mechanical properties of PLA/BF composites. Alkali treatment removed the small molecular compounds from BF, decreased its thermal stability, and increased the crystalline region and crystallinity of cellulose. Meanwhile, alkali treatment made BF fibrillated and increased its contactable active area with the coupling agents, but destructed the nature structure of BF. The silane coupling agent played a more important role than alkali treatment did in improving the interfacial compatibility of PLA/BF composites.

Waste paper is often underutilized as a low-value recyclable resource and can be a potential source of cellulose nanofibers (CNFs) due to its rich cellulose content. Three different processes, low acid treatment, alkali treatment and bleaching treatment, were used to pretreat the waste paper in order to investigate the effect of different pretreatments on the prepared CNFs, and CNFs obtained from bleached pulp boards were used as control. All sample fibers were successfully prepared into CNFs by 2,2,6,6-tetramethyl-piperidine-1-oxyl (TEMPO) oxidation. It was quite obvious that the bleached CNFs samples showed dense fibrous structures on a scanning electron microscopy (SEM), while needle-like fibers with width less than 20 nm were observed on a transmission electron microscopy (TEM). Meanwhile, the bleaching treatment resulted in a 13.5% increase in crystallinity and a higher TEMPO yield (e.g., BCNF, 60.88%), but a decrease in thermal stability. All pretreated CNFs samples showed narrow particle size distribution, good dispersion stability (zeta potential less than −29.58 mV), good light transmission (higher than 86.5%) and low haze parameters (lower than 3.92%). This provides a good process option and pathway for scalable production of CNFs from waste papers.

The article presents the preparation of a high-performance wood–plastic composites with improved interfacial interactions by adding ternary-monomer graft copolymers as the interfacial modifiers and by braising wood flour (WF) and investigates their effects on the rheological properties of recycled polyethylene (rPE)/WF composites. The processing properties, capillary rheological properties, dynamical rheological properties, and mechanical properties were investigated. Results show that graft copolymer of polyethylene is effective in improving the interfacial interactions of rPE/WF composites, dramatically changing the rheological and mechanical properties. The braising of WF enlarges the gaps of cells and promotes the infiltration of rPE into the gaps, as promoting the increasing in mechanical properties of rPE/WF composites and significantly changing the rheological properties of the composites.

Sisal fiber (SF) is a good raw material to prepare natural fiber composites (NFCs) by blending it with plastics. However, most NFCs are highly filled with natural fibers in order to decrease the cost of products that causes the weak interfacial compatibilities between the natural fibers and polymers. To successfully prepare a high-performance NFC, the interfacial compatibility is the key problem that should be disposed. In this paper, the graft copolymers of polyethylene (GPE) were used as the infiltrative compatibilizers for SF-filled recycled polyethylene (rPE) composites. How GPE affected the interfacial compatibility and performances of rPE/SF composites were investigated. Results show that the mechanical properties, water resistance and thermal stability of the composites increased with the increase in GPE. The improved interfacial interactions restrained the movement of rPE chains, resulting in the decreasing of crystallinity of the composites. GPE were favorable to improve the rheological properties of the composites. The scanning electron microscopy observation discovered that GPE promoted the formation of infiltrative interfacial interactions that primarily came from the chemical and physical interactions between SF and GPE.