Some α + β’ brass components of drinking water distribution systems in Morocco underwent early failures and were investigated to assess the nature and extent of the corrosion attacks. They exhibited different corrosion forms, often accompanied by extensive β’ dezincification. In order to offer viable alternatives to these traditional low cost materials, the corrosion behavior of two representative α + β’ brass components was compared to that of brass alloys with nominal compositions CuZn36Pb2As and CuZn21Si3P, marketed as dezincification resistant. CuZn21Si3P is a recently developed eco-friendly brass produced without any arsenic or lead. Electrochemical tests in simulated drinking water showed that after 10 days of immersion CuZn21Si3P exhibited the highest polarization resistance (R_p) values but after longer immersion periods its R_p values became comparable or lower than those of the other alloys. After 150 days, scanning electron microscope coupled to energy dispersive spectroscopy (SEM-EDS) analyses evidenced that the highest dezincification resistance was afforded by CuZn36Pb2As (longitudinal section of extruded bar), exhibiting dealloying and subsequent oxidation of β’ only at a small depth. Limited surface dealloying was also found on CuZn21Si3P, which underwent selective silicon and zinc dissolution and negligible inner oxidation of both α and κ constituent phases, likely due to peculiar galvanic effects.

Duplex α + β’ brasses are widely used in drinking water distribution systems for tube fittings, valves, and ancillaries because they are low cost, easy to fabricate, and exhibit high mechanical strength. However, depending on application conditions and alloy composition, they may undergo dealloying and stress corrosion cracking. In this research, three different brass types, two leaded (CW617N and CW602N) alloys and one lead-free brass (CW724R), were investigated to assess their corrosion behavior and susceptibility to stress corrosion cracking (SCC) in simulated drinking water (SDW) solutions containing different chloride concentrations, compatible with drinking water composition requirements according to Moroccan standard NM 03.7.001. The corrosion behavior was assessed by electrochemical tests such as polarization curve recording and electrochemical impedance spectroscopy (EIS) monitoring, coupled to SEM-EDS surface observations. The susceptibility to SCC was investigated by slow strain rate tests (SSRT). The tests showed that corrosion was mainly under diffusion control and chlorides slightly accelerated corrosion rates. All alloys, and particularly CW617N, were affected by SCC under the testing conditions adopted and in general the SCC susceptibility increased at increasing chloride concentration.