This article presents a novel potential bio-based rejuvenator derived from waste pig fat (WPF) for use in recycled asphalt applications. To achieve this purpose, the impact of different doses waste pig fat (e.g., 0, 3, 6, and 9 wt.% WPF) on the reclaimed asphalt pavement binder (RAP-B) performance is investigated. The unmodified and WPF-modified asphalts are characterized by means of Fourier-transform infrared spectroscopy (FT-IR), thin-layer chromatography–flame ionization detection (TLC-FID), scanning electron microscopy (SEM), atomic force microscopy (AFM), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). Physico-rheological properties of asphalt blends are assessed through Brookfield viscometer, softening point, penetration, and dynamic shear rheometer (DSR) tests. TLC-FID data highlighted that incremental WPF addition into RAP-B restored its original balance maltenes-to-asphaltenes ratio; finding which was supported by FT-IR analysis. SEM disclosed that WPF has a great compatibility with the aged asphalt. AFM observations showed that grease treatment induced a decline in surface roughness (i.e., bee structures) and a rise in friction force (i.e., para-phase dimension) of RAP binder. TGA/DSC studies revealed that the bio-modifier not only possesses an excellent thermal stability but also can substantially enhance the binder low-temperature performance. Empirical and DSR tests demonstrated that WPF improved the low-temperature performance grade of RAP-B, reduced its mixing and compaction temperatures, and noticeably boosted its fatigue cracking resistance. The rejuvenation of aged asphalt employing WPF is feasible and can be an ideal approach to recycle both of RAP and waste pig fats.

Thermally grown surface oxide layers dominate the single-asperity tribological behavior of a Zr₆₀Cu₃₀Al₁₀ glass. Increase in oxidation time leads to an increased contribution of shearing and a corresponding decreased contribution of ploughing to friction. This change in the dominating friction and wear mechanism results in an overall minor decrease of the friction coefficient of oxidized surfaces compared to the metallic glass sample with native surface oxide. Our results demonstrate the importance of creating a stable oxide layer for practical applications of metallic glasses in micro-devices involving sliding contact.

We report on the anelastic behavior of a cyclically loaded Zr_62.5Fe₅Cu_22.5Al₁₀ bulk metallic glass well below its yield strength. The dynamic mechanical behavior of the glass is discussed on the basis of its structural and thermodynamic properties before and after tests. We show how the kinetically frozen anelastic deformation accumulates at room temperature and causes a structural relaxation and densification of the glass and further leads to its partial crystallization.

We have investigated the sliding friction behavior of metallic couples with different enthalpy of mixing or reaction by friction force microscopy. Comparing the friction behavior of miscible and immiscible couples we find that in the first case friction is governed by adhesion while the shear strength is low (τ = 3–6 MPa). In the latter case of immiscible couples, adhesion is found to be low and the shear strength is large (τ ≈ 70 MPa). Statistical analysis of atomic stick-slip images recorded on an Au(111) surface with tips of different affinities with gold allows for a deeper understanding of our results. The periodicity of atomic stick-slip images corresponds to the interatomic distance of gold for immiscible counter-bodies. In contrast, for a reactive couple the periodicity of atomic stick-slip significantly differs from the gold interatomic distance and may correspond to the structural length of an ordered intermediate phase at the tip-surface interface.