The tribological behaviors of graphene and graphene oxide (GO) as water-based lubricant additives were evaluated by use of a reciprocating ball-on-plate tribometer for magnesium alloy-steel contacts. Three sets of test conditions were examined to investigate the effect of concentration, the capacity of carrying load and the endurance of the lubrication film, respectively. The results showed that the tribological behaviors of water can be improved by adding the appropriate graphene or GO. Compared with pure deionized water, 0.5 wt.% graphene nanofluids can offer reduction of friction coefficient by 21.9% and reduction of wear rate by 13.5%. Meanwhile, 0.5 wt.% GO nanofluids were found to reduce the friction coefficient and wear rate up to 77.5% and 90%, respectively. Besides this, the positive effect of the GO nanofluids was also more pronounced in terms of the load-carrying capacity and the lubrication film endurance. The wear mechanisms have been tentatively proposed according to the observation of the worn surfaces by field emission scanning electron microscope-energy dispersive spectrometer (FESEM-EDS) and Raman spectrum as well as the wettability of the nanofluids on the magnesium alloy surface by goniometer.

The tribological performances of the SiO₂/MoS₂ hybrids as lubricant additives were explored by a reciprocating ball-on-flat tribometer for AZ31 magnesium alloy/AISI 52100 bearing steel pairs. The results demonstrated that the introduction of SiO₂/MoS₂ hybrids into the base oil exhibited a significant reduction in the friction coefficient and wear volume as well as an increase in load bearing capacity, which was better than the testing results of the SiO₂ or MoS₂ nanolubricants. Specifically, the addition of 0.1 wt % nano-SiO₂ mixed with 1.0 wt % nano-MoS₂ into the base oil reduced the friction coefficient by 21.8% and the wear volume by 8.6% compared to the 1.0 wt % MoS₂ nanolubricants. The excellent lubrication behaviors of the SiO₂/MoS₂ hybrid nanolubricants can be explained by the micro-cooperation of different nanoparticles with disparate morphology and lubrication mechanisms.

The tribological performances of fullerenol and nanodiamonds (NDs) as additives in water-based lubricants for amorphous carbon (a-C) coatings are investigated to avoid disadvantage factors, such as chemical reactions and deformation of particles. The effects of size and additive amount on tribological properties of nanoparticles are studied by rigid nanoparticles within the dot size range. The results show that owing to its small particle size (1–2 nm), fullerenol cannot prevent direct contact of the friction pair at low concentration conditions. Only when the quantity of fullerenol increased to support the asperity contact loads in sufficient concentration did nano-bearings perform well in anti-friction and anti-wear effects. Unlike fullerenol, nanodiamond particles with a diameter of about 5–10 nm show friction-reducing effect based on the nano-bearing effects at ultra-low concentration (0.01 wt.%), whereas particles at higher concentration block the rolling movement, hence increasing the coefficient of friction (COF) and wear. As a result of the effect of difference in size, fullerenol provides a better overall lubrication, but it is hard to reach a friction coefficient as low as NDs even under the optimal conditions.

Microstructures and mechanical properties of Mg-9Al/Ti metallurgical bonding prepared by liquid-solid diffusion couples were investigated. The results indicate that a metallurgical bonding was formed at the interface Mg-9Al/Ti, and the Mg₁₇Al₁₂ phase growth coarsening at the interfaces with the increase in heat treatment time. Push-out testing was used to investigate the shear strength of the Mg-9Al/Ti metallurgical bonding. It is shown that the shear strength presents an increasing tendency with the increased heat treatment time. The sequence is characterized, and the results show that the fracture takes place along the Mg-9Al matrix at the interface. The diffusion of Al and Ti elements play a dominant role in the interface reaction of Mg-9Al/Ti metallurgical bonding. By energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD) and thermodynamic analysis, it was found that Al₃Ti is the only intermetallic compound at the interface of Mg-9Al/Ti metallurgical bonding. These results clearly show that chemical interaction at the interface formation of Al₃Ti improves the mechanical properties of Mg-9Al/Ti metallurgical bonding.

To improve the electrochromic (EC) properties of sol–gel-derived WO₃ films, a series of organic small molecules, such as dopamine (DA), catechol, tyramine, phenol and 2-phenylethylamine, were added into peroxotungstic acid precursor sols as structure-directing additives, and five modified WO₃ films were prepared by a simple and low-cost complexation-assisted sol–gel method. The effects of the above additives on the EC properties of the modified WO₃ films have been studied in detail. Compared with the pure WO₃ polycrystalline film, all the modified films combine the advantages of nanocrystalline and amorphous phases and show higher EC properties attributed to the unique nanocrystal-embedded amorphous structure. The results indicate that different additives with different numbers and types of functional groups (hydroxyl and amino groups) can change the microstructure, morphology, and thus electrochemical and EC properties of the films in various degrees. The additives, in order of their strong interactions with the sols, are DA, catechol, tyramine, phenol and 2-phenylethylamine, primarily depending on the number of hydroxyl groups. Of all the additives, DA with both catechol hydroxyl and amino groups shows the most positive effect; that is, the WO₃ film modified with DA exhibits the best EC properties in terms of contrast, switching speed, stability, and coloration efficiency.