Melanin denotes a variety of mammalian pigments, including the dark electrically conductive eumelanin and the reddish, sulfur-containing, pheomelanin. Organic (bio)electronics is showing increasing interests in eumelanin exploitation, e.g., for bio-interfaces, but the low conductivity of the material is limiting the development of eumelanin-based devices. Here, for the first time, we report an abrupt increase of the eumelanin electrical conductivity, revealing the highest value presented to date of 318 S/cm. This result, obtained via simple thermal annealing in vacuum of the material, designed on the base of the knowledge of the eumelanin chemical properties, also discloses the actual electronic nature of this material's conduction.

Highly sensitive alternate current (ac) impedance measurements with variable temperature have been performed to investigate the optical and electrical failure mechanisms during the glass transition phenomena in the archetypal $\text{ITO}/\text{TPD}/{\text{Alq}}_3/\text{Al}$ organic light emitting diode (OLED) structure. Since the device degradation is mainly related to the lower glass transition temperature $\left(T_g\right)$ of the $N,N^{\prime }$ -Bis(3-methylphenyl)-$N,N^{\prime }$ -diphenylbenzidine (TPD), this study is focused on the frequency response of thin TPD films approaching the glassy region. The related experimental data are discussed in the framework of the universal dielectric response model. By ac measurements, TPD glass transition temperature is located and temperature regions with different OLED behaviors are evidenced. The relation between the behaviors of TPD frequency response and of the OLED electro-optical response, while the temperature approaches the glass transition region, is discussed.

In this paper, we present a new type of parallax barrier, for switchable 2D/3D display vision, obtained by using a Reverse Mode Polymer Dispersed Liquid Crystal display (RV-PDLC). The parallax barrier was prepared by sandwiching the RV-PDLC film between two ITO conductive glass supports. Strips of ITO were removed from one of the supports, in order to alternate conductive to not conductive strips. In this way the RV-PDLC films could be electrically switched in a parallax barrier able to turn a 2D image in a 3D one. The RV-PDLC barrier was obtained in tree steps: (1) a nematic diacrylate monomer (NDM) was dissolved in a nematic liquid crystal (NLC) in the presence of a small quantity of radical polymerisation initiator; (2) the mixture was homeotropically aligned between the glass conductive supports, previously treated with an aligning chemical; (3) the liquid crystal monomer was polymerised by UV curing. A 2D/3D switchable device was finally obtained by coupling the parallax barrier with a 2D tablet display. GRAPHICAL ABSTRACT