Complicated wear-resistant parts made by selective laser melting (SLM) of powder material based on compositions of metal and ceramics can be widely used in mining, oil engineering, and other precision engineering industries. Ceramic–metal compositions were made using nanoscale powders by powder metallurgy methods. Optimal regimes were found for the SLM method. Chemical and phase composition, fracture toughness, and wear resistance of the obtained materials were determined. The wear rate of samples from 94 wt% tungsten carbide (WC) and 6 wt% cobalt (Co) was 1.3 times lower than that of a sample from BK6 obtained by the conventional methods. The hardness of obtained samples 2500 HV was 1.6 times higher than that of a sample from BK6 obtained by the traditional method (1550 HV).

Additive manufacturing of polymer products over the past decade has become widespread in various areas of industry. Using the fused filament fabrication (FFF) method, one of the most technologically simple methods of additive manufacturing, it is possible to produce parts from a large number of different materials, including wear-resistant nylon. The novelty of the work is properties investigation of ±45° filling configuration with different filling degree for nylon, as well as calculating the effect of infill on the strength characteristics, excluding the shell. This article reflects the process of manufacturing samples from nylon using FFF technology with various internal topologies, as well as tensile tests. The analysis of the obtained results is performed and the relationship between the structure of the sample and the limit of its strength is established. To calculate real filling degree and the effect of internal filling on the strength characteristics of the specimen, it is proposed to use a method based on the geometric and mass parameters. The FFF method is promising for developing methods for producing a composite material. The results of this article can be useful in choosing the necessary manufacturing parameters.

Additive manufacturing methods make it possible to create complex geometry parts, that cannot be produced by conventional methods. For manufacture of the products, composite polymeric materials can be used, both disperse-filled and filled with short or continuous fibers. Recently, more and more attention has been paid to reinforcing plastics with natural fibers. The study of the manufacturing process of a polymeric composite material filled with continuous natural fibers by the fused filament fabrication is presented