Complicated wear-resistant parts made by selective laser melting (SLM) of powder material based on compositions of metal and ceramics can be widely used in mining, oil engineering, and other precision engineering industries. Ceramic–metal compositions were made using nanoscale powders by powder metallurgy methods. Optimal regimes were found for the SLM method. Chemical and phase composition, fracture toughness, and wear resistance of the obtained materials were determined. The wear rate of samples from 94 wt% tungsten carbide (WC) and 6 wt% cobalt (Co) was 1.3 times lower than that of a sample from BK6 obtained by the conventional methods. The hardness of obtained samples 2500 HV was 1.6 times higher than that of a sample from BK6 obtained by the traditional method (1550 HV).

Additive manufacturing of polymer products over the past decade has become widespread in various areas of industry. Using the fused filament fabrication (FFF) method, one of the most technologically simple methods of additive manufacturing, it is possible to produce parts from a large number of different materials, including wear-resistant nylon. The novelty of the work is properties investigation of ±45° filling configuration with different filling degree for nylon, as well as calculating the effect of infill on the strength characteristics, excluding the shell. This article reflects the process of manufacturing samples from nylon using FFF technology with various internal topologies, as well as tensile tests. The analysis of the obtained results is performed and the relationship between the structure of the sample and the limit of its strength is established. To calculate real filling degree and the effect of internal filling on the strength characteristics of the specimen, it is proposed to use a method based on the geometric and mass parameters. The FFF method is promising for developing methods for producing a composite material. The results of this article can be useful in choosing the necessary manufacturing parameters.

A uniform distribution of power density (energy flux) in a stationary laser beam leads to a decrease in the overheating of the material in the center of the laser beam spot during laser powder bed fusion and a decrease in material losses due to its thermal ablation and chemical decomposition. The profile of the uniform cylindrical (flat-top) distribution of the laser beam power density was compared to the classical Gaussian mode (TEM₀₀) and inverse Gaussian (donut) distribution (airy distribution of the first harmonic, TEM_01* = TEM₀₁ + TEM₁₀). Calculation of the Péclet number, which is a similarity criterion characterizing the relationship between convective and molecular processes of heat transfer (convection to diffusion) in a material flow in the liquid phase, shows that the cylindrical (flat-top) distribution (TEM_01* + TEM₀₀ mode) is effective in a narrow temperature range. TEM₀₀ shows the most effective result for a wide range of temperatures, and TEM_01* is an intermediate in which evaporation losses decrease by more than 2.5 times, and it increases the absolute laser bandwidth when the relative bandwidth decreases by 24%.

Phase composition and microstructure of initial WC, BK8 (powder alloy 92 wt.% WC–8 wt.% Co), Co powders, ball-milled powders with four different compositions (1) 25 wt.% WC–75 wt.% Co, (2) 30 wt.% BK8–70 wt.% Co, (3) 50 wt.% WC–50 wt.% Co, (4) 94 wt.% WC–6 wt.% Co, and bulk alloys obtained by selective laser melting (SLM) from as-milled powders in as-melted state and after heat treatment were investigated by scanning electron microscopy and X-ray diffraction analysis. Initial and ball-milled powders consist of WC, hexagonal α-Co and face-centered cubic β-Co. The SLM leads to the formation of major new phases W3Co3C, W4Co2C and face-centered cubic β-Co-based solid solution. During the heat treatment, there occurs partial decomposition of the face-centered cubic β-Co-based solid solution with the formation of W2C and hexagonal α-Co solid solution. The microstructure of obtained bulk samples, in general, corresponds to the observed phase composition.