High-quality single-crystal diamond films, homoepitaxially grown by microwave chemical vapor deposition, have been used to produce diamond-based photodetectors. Such devices were tested over a very wide spectral range, from the extreme ultraviolet (UV) (20 nm) up to the near IR region (2400 nm). An optical parametric oscillator tunable laser was used to investigate the 210–2400 nm spectral range in pulse mode. In this region, the spectral response shows a UV to visible contrast of about 6 orders of magnitude. A time response shorter than 5 ns, i.e., the laser pulse duration, was observed. By integrating the pulse shape, a minor slow component was evidenced, which can be explained in terms of trapping–detrapping effects. Extreme UV gas sources and a toroidal grating vacuum monochromator were used to measure the device response down to 20 nm in continuous mode. In particular, the extreme UV He spectrum was measured and the He II m, 30.4 nmand He I 58.4 nm emission lines were clearly detected. The measured time response of 0.2 s is totally due to the instrumental readout time constants. In both experimental setups an extremely good stability and reproducibility of the device response were obtained, whereas no persistent photoconductivity nor undesirable pumping effects were observed.

Purpose: FLASH radiotherapy (RT) is an emerging technique in which beams with ultra‐high dose rates (UH‐DR) and dose per pulse (UH‐DPP) are used. Commercially available active real‐time dosimeters have been shown to be unsuitable in such conditions, due to severe response nonlinearities. In the present study, a novel diamond‐based Schottky diode detector was specifically designed and realized to match the stringent requirements of FLASH‐RT.Methods: A systematic investigation of the main features affecting the diamond response in UH‐DPP conditions was carried out. Several diamond Schottky diode detector prototypes with different layouts were produced at Rome Tor Vergata University in cooperation with PTW‐Freiburg. Such devices were tested under electron UH‐DPP beams. The linearity of the prototypes was investigated up to DPPs of about 26 Gy/pulse and dose rates of approximately 1 kGy/s. In addition, percentage depth dose (PDD) measurements were performed in different irradiation conditions. Radiochromic films were used for reference dosimetry.Results: The response linearity of the diamond prototypes was shown to be strongly affected by the size of their active volume as well as by their series resistance. By properly tuning the design layout, the detector response was found to be linear up to at least 20 Gy/pulse, well into the UH‐DPP range conditions. PDD measurements were performed by three different linac applicators, characterized by DPP values at the point of maximum dose of 3.5, 17.2, and 20.6 Gy/pulse, respectively. The very good superimposition of three curves confirmed the diamond response linearity. It is worth mentioning that UH‐DPP irradiation conditions may lead to instantaneous detector currents as high as several mA, thus possibly exceeding the electrometer specifications. This issue was properly addressed in the case of the PTW UNIDOS electrometers.Conclusions: The results of the present study clearly demonstrate the feasibility of a diamond detector for FLASH‐RT applications.

We report on a systematic investigation of the properties of long Josephson junctions under the application of magnetic fields generating Fiske and Eck steps in the current-voltage characteristics. Numerical data and experimental results are compared with a cavity mode-based model predicting the voltage position and the amplitude of the current singularities. The comparison shows that this model can account for the shape and for the maximum current modulation of the singularities when the field penetration overcomes Meissner shielding above the value $H_0=2\mathrm{}{\lambda }_j{j}_c.$

Recently, solid state photovoltaic Schottky diodes, able to detect ionizing radiation, in particular, x-ray and ultraviolet radiation, have been developed at the University of Rome “Tor Vergata.” We report on a physical and electrical properties analysis of the device and a detailed study of its detection capabilities as determined by its electrical properties. The design of the device is based on a metal/nominally intrinsic/p-type diamond layered structure obtained by microwave plasma chemical vapor deposition of homoepitaxial single crystal diamond followed by thermal evaporation of a metallic contact. The device can operate in an unbiased mode by using the built-in potential arising from the electrode-diamond junction. We compare the expected response of the device to photons of various energies calculated through Monte Carlo simulation with experimental data collected in a well controlled experimental setup i.e., monochromatic high flux x-ray beams from 6 to 20 keV, available at the Diamond Light Source synchrotron in Harwell (U.K.).

We report on a comparative study of transfer doping of hydrogenated single crystal diamond surface by insulators featured by high electron affinity, such as Nb₂O₅, WO₃, V₂O₅, and MoO₃. The low electron affinity Al₂O₃ was also investigated for comparison. Hole transport properties were evaluated in the passivated hydrogenated diamond films by Hall effect measurements, and were compared to un-passivated diamond films (air-induced doping). A drastic improvement was observed in passivated samples in terms of conductivity, stability with time, and resistance to high temperatures. The efficiency of the investigated insulators, as electron accepting materials in hydrogenated diamond surface, is consistent with their electronic structure. These surface acceptor materials generate a higher hole sheet concentration, up to 6.5 × 10¹³ cm⁻², and a lower sheet resistance, down to 2.6 kΩ/sq, in comparison to the atmosphere-induced values of about 1 × 10¹³ cm⁻² and 10 kΩ/sq, respectively. On the other hand, hole mobilities were reduced by using high electron affinity insulator dopants. Hole mobility as a function of hole concentration in a hydrogenated diamond layer was also investigated, showing a well-defined monotonically decreasing trend.