The surface, corrosion and wear properties of new and in vivo exposed nickel titanium (NiTi) and stainless steel (SS) archwires used in orthodontic treatment were investigated. Electrochemical and tribo-electrochemical tests in artificial saliva were performed in order to define corrosion properties and to estimate wear rate of new and in vivo exposed NiTi and SS archwires. The surface chemical analysis of the passive film on the NiTi and SS archwires before and after tribocorrosion tests was performed by Auger Electron Spectroscopy (AES). In vivo exposed NiTi and SS archwires had better electrochemical properties than new archwires due to the protective nature of oral deposits. Total wear and coefficients of friction were higher among in vivo exposed archwires and higher in NiTi archwires in comparison to SS archwires. The estimated thickness of the TiO₂ passive film on as-received NiTi is 8 nm, while the passive Cr₂O₃ film on as-received SS is just 1–2 nm. On in vivo exposed NiTi archwire, a 60–80 nm thick organic film/dental plaque was observed, and on SS, it was thinner, at about 60 nm. This research shows the importance of combining AES with electrochemical testing, to characterize tribocorrosive properties of NiTi and SS orthodontic archwires.

Nickel-titanium (NiTi) orthodontic archwires are crucial in the initial stages of orthodontic therapy when the movement of teeth and deflection of the archwire are the largest. Their great mechanical properties come with their main disadvantage—the leakage of nickel. Various in vitro studies measured nickel leakage from archwires that were only immersed in the medium with little or minimal simulation of all stress and deflection forces that affect them. This study aims to overcome that by simulating deflection forces that those archwires are exposed to inside the mouth of a patient. NiTi orthodontic archwires were immersed in CACO2-2 cell culture medium and then immediately loaded while using a simulator of multiaxial stress for 24 h. After the experiment, the surface of the NiTi orthodontic archwires were analysed while using scanning electron microscopy (SEM) and auger electron spectroscopy (AES). The observations showed significant microstructural and compositional changes within the first 51 nm thickness of the archwire surface. Furthermore, the released nickel and titanium concentrations in the CACO2-2 cell culture medium were measured while using Inductively Coupled Plasma Mass Spectroscopy (ICP-MS). It was found out that the level of released nickel ions was 1.310 µg/L, which can be assigned as statistically significant results. These data represent the first mention of the already detectable release of Ni ions after 24 h during the simulation of mechanical loading in the CACO2-2 cell culture medium, which is important for clinical orthodontic praxis.

We have investigated new and retrieved cementless hip endoprostheses that prematurely failed due to (i) aseptic loosening, (ii) infection and (iii) latent infection. The aim was to better understand the physico-chemical phenomena on the surfaces and sub-surfaces of the Ti6Al7Nb alloy implant. The results of our studies should enable us to distinguish the causes of premature failure, optimize the surface modification, achieve optimal osseointegration and extend the useful lifetime of the implants. The surface properties of the Ti6Al7Nb alloys of the hip-stem endoprostheses (30 retrieved and 2 new) were determined by contact-angle measurements and the average surface roughness. The surface chemistry and microstructure were analysed by scanning electron microscopy (SEM) for morphology, energy-dispersive X-ray spectroscopy (EDS) for the chemistry, and electron back-scatter diffraction (EBSD) for the phase analysis; Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) for the surface chemistry; and electrochemical measurements for the corrosion. The improved wettability of the grit-blasted surface of the Ti6Al7Nb stems after autoclaving was measured, as was the super wettability after oxygen-plasma sterilization. The secondary-electron images showed that the morphology and microstructure of the new and retrieved stems (prematurely failed due to aseptic loosening, infection and latent infection) differ slightly, while the EDS analysis revealed corundum contamination of the grit-blasted surface. We found corundum-contaminated Ti6Al7Nb stem surfaces and sub-surfaces for all the investigated new and retrieved implants. These residues are a potential problem, i.e., third-body wear particles, and probably induce the osteolysis and aseptic loosening.

For the improvement of surface roughness, titanium joint arthroplasty (TJA) components are grit-blasted with Al₂O₃ (corundum) particles during manufacturing. There is an acute concern, particularly with uncemented implants, about polymeric, metallic, and corundum debris generation and accumulation in TJA, and its association with osteolysis and implant loosening. The surface morphology, chemistry, phase analysis, and surface chemistry of retrieved and new Al₂O₃ grit-blasted titanium alloy were determined with scanning electron microscopy (SEM), X-ray energy-dispersive spectroscopy (EDS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and confocal laser fluorescence microscopy, respectively. Peri-prosthetic soft tissue was studied with histopathology. Blasted retrieved and new stems were exposed to human mesenchymal stromal stem cells (BMSCs) for 7 days to test biocompatibility and cytotoxicity. We found metallic particles in the peri-prosthetic soft tissue. Ti6Al7Nb with the residual Al₂O₃ particles exhibited a low cytotoxic effect while polished titanium and ceramic disks exhibited no cytotoxic effect. None of the tested materials caused cell death or even a zone of inhibition. Our results indicate a possible biological effect of the blasting debris; however, we found no significant toxicity with these materials. Further studies on the optimal size and properties of the blasting particles are indicated for minimizing their adverse biological effects.