The aims of this study were to investigate how the release of tadalafil is influenced by two grades of polyvinylpyrrolidone (Kollidon^® 12 PF and Kollidon^® VA 64) and various methods of preparing solid dispersions (solvent evaporation, spray drying and hot-melt extrusion). Tadalafil is poorly water-soluble and its high melting point makes it very sensitive to the solid dispersion preparation method. Therefore, the objectives were to make a comparative evaluation among different solid dispersions and to assess the effect of the physicochemical nature of solid dispersions on the drug release profile with respect to the erosion-diffusion mechanism. The solid dispersions were evaluated for dissolution profiles, XRD, SEM, FT-IR, DSC, and solubility or stability studies. It was found that tadalafil release was influenced by polymer molecular weight. Therefore, solid dispersions containing Kollidon^® 12 PF showed a faster dissolution rate compared to Kollidon^® VA 64. Tadalafil was released from solid dispersions containing Kollidon^® 12 PF because of the combination of erosion and diffusion mechanisms. The diffusion mechanisms were predominant in the initial phase of the experiment and the slow erosion was dissolution-controlling at the second stage of the dissolution. On the contrary, the tadalafil release rate from solid dispersions containing Kollidon^® VA 64 was controlled solely by the erosion mechanism.

Zinc and its alloys seem to be promising candidates for biodegradable applications. Those materials are often modified by other elements or compounds in order to enhance their properties. The combination of zinc and apatites is challenging for several reasons. However, the advantages connected with the biological aspects suggest the need for further research into such materials. In this study, three zinc-based composites with 4 and 8 wt. % of nanohydroxyapatite or nanomonetite (Zn-4MO, Zn-4HA, Zn-8HA) were prepared by sintering and subsequent extrusion. Materials prepared in this way were characterized from the microstructural, mechanical and corrosion point of view. The obtained results showed a significant influence of particle character (amount and morphology) on the strength and ductility of the prepared materials. In case of Zn-4MO, the presence of monetite significantly increased the ductility compared with the other materials. In addition, the increment of the degradation rate caused by the presence of monetite was observed as well. All obtained results pointed out to significant advantages of monetite for the preparation of Zn-apatite composites compared with hydroxyapatite.