The generation of a nickel-reduced, stainless spring steel strip with a thickness of 0.2 mm, producible under industrial conditions, is the aim of a transfer project together with the Institute of Metal Forming/TU BAF and the Auerhammer Metallwerk GmbH within the DFG Collaborative Research Centre (CRC) 799. The spring steel strip should exhibit a tensile strength of ≥1700 MPa in work-hardened and partitioned state. The mechanical and corrosive properties of the steel strip should be equal or better than those given for 1.4310 steel (AISI 301). The article presents the results of laboratory alloys focused on the design of steel strips, which meet the requirements for a cost-effective production. The results presented relate to steel design, microstructure formation, temperature-dependent mechanical properties, and corrosion resistance. Four alloys of the type X5CrMnNiMoN16-x-4 with manganese contents of approximately 2 to 6 wt.-percent were investigated. The austenitic steel X5CrMnNiMoN16-4-4 with TRIP/TWIP effect was selected for deformation and partitioning treatments. Its deformation-induced α’-martensite formation significantly contributes to the work hardening of the steel. A short-time annealing treatment (partitioning) further increases the strength properties.

The article presents the mechanical properties of the austenitic stainless steel X5CrMnNiMoN16-4-4 after deformation by cold rolling and subsequent short-term tempering (deformation and partitioning (D&P) treatment). Tensile strengths of 1700–900 MPa and beyond were achieved both after work hardening and in the D&P-treated strip. The initial state of austenite in terms of grain size and pre-strengthening, as well as the selected cold rolling temperature significantly influenced the deformation-induced formation of α’ martensite and thus the flow and hardening behavior of the steel. The usage of two different rolling temperature regimes showed that the strength properties in the cold strip can be specifically adjusted. Lower deformation-induced martensite fractions enabled a larger thickness reduction of the strip without increasing the rolling force, while high deformation-induced martensite fractions led to strong hardening at low deformation levels. The D&P-treatment permits the strength of the cold-rolled strip with a predominantly austenitic microstructure to be increased to the required level. The total elongation of such a D&P strip was well over 2%. The D&P treatment of the spring steel strip is a cost-effective alternative to conventional tempering treatment.