Samples of 6082-T6 aluminum alloy were welded by bobbin tool friction stir welding at different rotational speeds. The thermal cycles, microstructure, microhardness, and tensile properties of the specimens were investigated. The results show that the maximum temperature at the joint increases first and then decreases with increasing rotational speed, and the maximum temperature is 509 °C at 1000 r/min. The macromorphology of the cross-section of the joint is rectangular, and an ‘’S” line and gray-white texture can be observed. The stirred zone had much smaller equiaxed recrystallized grains. With increasing welding speed, the average grain size in the stirred zone region decreases. The microhardness distribution of the cross-section of all joints is W-shaped. When the rotational speed increases, the hardness of the heat-affected zone decreases gradually, and the hardness of the stirred zone increases. At 600 r/min, the strength is the lowest. The fracture location is between the stirred zone and the thermomechanically affected zone. When the rotational speed is increased, the fracture location is entirely located in the heat affected zone, and the fracture surface is dimple-like; the strength significantly increases and reaches a maximum at 800 r/min.

With the rapid development of various industries, the connection of copper and aluminum is in high demand. However, as a solid-phase connection technology, friction stir welding has a potential application prospect in the connection of copper and aluminum. This paper comprehensively summarizes the most recent 20 years of the literature related to the friction stir welding of copper and aluminum. The application significance of copper and aluminum connectors is introduced, and the research field of the friction stir welding of copper and aluminum is analyzed and explored from the aspects of welding technology, microstructure and mechanical properties, as well as innovations and improvements in the welding process. In view of the research status of this field, the authors put forward their views and prospects for its future, aiming to provide a basis for researchers in this field.

In this paper, the effect of different shapes of tool pin on the plastic flow of 2024-T6 aluminum alloy during friction stir welding was studied. In order to observe the plastic flow of materials more clearly, we chose the method of friction stir welding of dissimilar materials, considering the different corrosive characteristics of aluminum alloys made of different materials when exposed to the same corrosive liquid. By studying and comparing the temperature field, macro and microstructure, microhardness and tensile properties of welded joints, the results indicated that the metal in the weld nugget zone (WNZ) mainly came from the base metal of the advancing side, the thread being the driving force of the downward movement of the FSW plastic metal. The deep groove thread tool pin had the strongest ability to drive the metal downward. The conical cam thread tool pin had the strongest stirring effect on materials and the best metal fluidity. The macroscopic morphology, microstructure, mechanical properties and fracture morphology of different joints were analyzed, and the results showed that all joints could form an excellent union, with an onion ring pattern appearing in cross-section. The minimum grain size of the WNZ formed by the conical cam thread stirring head was 7~12 μm; the hardness was least at the junction of the heat affected zone (HAZ) and the thermo-mechanically affected zone (TMAZ). However, the hardness of the weld formed by the conical cam thread at this point was higher than that of other stirring heads; the tensile strength of all joints was more than 80% of the BM, and the maximum tensile strength of the joint welded by the conical cam thread tool pin was 364.27 MPa, accounting for 86.73% of the base metal (BM). The elongation after break was 14.95%. Tensile fracture morphology analysis showed that all joints were fractured by plastic fracture.

In this study, based on the principles of bionics, we fabricated a bionic non-smooth concave pit structure on the shoulders of friction stir welding tools and detected the thermal cycling curve, downforce, and torque of the tool in the welding process. We tested the wear loss weight and analyzed the surface morphology of the shoulder surfaces after welding for 200 m. This study found that as the distance between the concave pits decreased and the number of concave pits increased, the maximum downforce, torque, and temperature in the welding process showed a decreasing trend. As the speed increased, no matter how the tool structure changed, the downforce and torque decreased, while the peak thermal cycle temperature increased. The experimental welding results show that the wear loss weight of the non-smooth structure tool significantly reduced. The lowest wear loss weight of the tool with a concave pit interval of 1.125 mm was only 0.1529 g, which is 27% lower than that of the conventional tool. Our observations of the surface morphology of the tool shoulder after welding showed that the amount of aluminum swarf on the tool shoulder of the welding tool gradually declined with the increasing density of the uneven pits. The lowest number of aluminum chips adhered to a welding tool with a pit distance of 1.125 mm. Therefore, friction stir welding tools with biomimetic structures have better wear resistance and adhesion resistance.