A simple method is reported for the preparation of silver nanoparticle (AgNP) embedded pH-responsive hydrogel microparticle catalyst via Michael addition gelation and in-situ silver nitrate (AgNO₃) reduction. The AgNP-hydrogel microsphere exhibited an efficient reduction of pollutants like 4-Nitrophenol (4-NP) and Congo red (CR) under acidic medium with turn over frequency (TOF) of ~170 h^-1 and ~124 h^-1 respectively. Interestingly, the activity of the catalysts was turned-OFF under a basic medium (≥ pH 12) due to the deswelling pH-responsive matrix surrounding the AgNPs. On the contrary, turning-OFF the hydrogenation of a cationic pollutant like methylene blue (MB) using high pH (≥ 12) was not possible, due to ionic interaction of MB molecules with the negatively charged catalyst at this pH. This feature was used to demonstrate selective hydrogenation of only MB from a mixture of 4-NP and MB. Finally, five recycling steps confirmed the reusability and practical application potential of the catalyst.

Organic/inorganic hybrid composite materials with the dispersed phases in sizes down to a few tens of nanometers raised very great interest. In this paper, it is shown that silica/epoxy nanocomposites with a silica content of 6 wt % may be obtained with an “in situ” sol–gel procedure starting from two precursors: tetraethyl orthosilicate (TEOS) and 3-aminopropyl-triethoxysilane (APTES). APTES also played the role of a coupling agent. The use of advanced techniques (bright-field high-resolution transmission electron microscopy, HRTEM, and combined small- and wide-angle X-ray scattering (SAXS/WAXS) performed by means of a multirange device Ganesha 300 XL+) allowed us to evidence a multisheet structure of the nanoparticles instead of the gel one typically obtained through a sol–gel route. A mechanism combining in a new manner well-assessed knowledge regarding sol–gel chemistry, emulsion formation, and Ostwald ripening allowed us to give an explanation for the formation of the observed lamellar nanoparticles.