In this paper, for the first time, inexpensive waterglass solutions are exploited as a new, simple and ecofriendly chemical approach for promoting the formation of a silica-based coating on hemp fabrics, able to act as a thermal shield and to protect the latter from heat sources. Fourier Transform Infrared (FTIR) and solid-state Nuclear Magnetic Resonance (NMR) analysis confirm the formation of –C–O–Si– covalent bonds between the coating and the cellulosic substrate. The proposed waterglass treatment, which is resistant to washing, seems to be very effective for improving the fire behavior of hemp fabric/epoxy composites, also in combination with ammonium polyphosphate. In particular, the exploitation of hemp surface treatment and Ammonium Polyphosphate (APP) addition to epoxy favors a remarkable decrease of the Heat Release Rate (HRR), Total Heat Release (THR), Total Smoke Release (TSR) and Specific Extinction Area (SEA) (respectively by 83%, 35%, 45% and 44%) as compared to untreated hemp/epoxy composites, favoring the formation of a very stable char, as also assessed by Thermogravimetric Analysis (TGA). Because of the low interfacial adhesion between the fabrics and the epoxy matrix, the obtained composites show low strength and stiffness; however, the energy absorbed by the material is higher when using treated hemp. The presence of APP in the epoxy matrix does not affect the mechanical behavior of the composites.

Following a waste-to-wealth approach, humic acid (HA) was exploited as a flame retardant additive. The effect of its addition alone and in combination with urea (UR) and ammonium polyphosphate (APP) on the thermal, fire, and mechanical performances of a bisphenol A diglycidyl ether (DGEBA)-based epoxy resin modified with (3-aminopropyl)-triethoxysilane (AP) and cured with aliphatic isophoronediamine (IDA) has been investigated. Unlike in previous studies, a UL 94-V-0 classification was achieved for epoxy resin containing HA at 6 wt % and APP at only 1 wt % phosphorus (P) loading. The presence of silicon-modified epoxy chains ameliorated the distribution of the biowaste within the resin, and the addition of HA alone avoided melt dripping. Besides, APP and UR promoted a remarkable reduction (up to 52%) of the peak heat release rate (pHRR) values and a significant delay (up to 21%) of the time to ignition in cone calorimetry tests, and hence an increase (up to 1.8 min) of the time to flashover, without any detrimental effect on the overall mechanical behavior. The evolved gas, thermal, and fire analysis was used to propose the combined mode of action of HA, UR, APP, and silicon in the fire performance improvement of the hybrid epoxy system.

Thermosetting polymers have been widely used in many industrial applications as adhesives, coatings and laminated materials, among others. Recently, bisphenol A (BPA) has been banned as raw material for polymeric products, due to its harmful impact on human health. On the other hand, the use of aromatic amines as curing agents confers excellent thermal, mechanical and flame retardant properties to the final product, although they are toxic and subject to governmental restrictions. In this context, sugar-derived diepoxy monomers and anhydrides represent a sustainable greener alternative to BPA and aromatic amines. Herein, we report an “in-situ” sol–gel synthesis, using as precursors tetraethylorthosilicate (TEOS) and aminopropyl triethoxysilane (APTS) to obtain bio-based epoxy/silica composites; in a first step, the APTS was left to react with 2,5-bis[(oxyran-2-ylmethoxy)methyl]furan (BOMF) or diglycidyl ether of bisphenol A (DGEBA)monomers, and silica particles were generated in the epoxy in a second step; both systems were cured with methyl nadic anhydride (MNA). Morphological investigation of the composites through transmission electron microscopy (TEM) demonstrated that the hybrid strategy allows a very fine distribution of silica nanoparticles (at nanometric level) to be achieved within a hybrid network structure for both the diepoxy monomers. Concerning the fire behavior, as assessed in vertical flame spread tests, the use of anhydride curing agent prevented melt dripping phenomena and provided high char-forming character to the bio-based epoxy systems and their phenyl analog. In addition, forced combustion tests showed that the use of anhydride hardener instead of aliphatic polyamine results in a remarkable decrease of heat release rate. An overall decrease of the smoke parameters, which is highly desirable in a context of greater fire safety was observed in the case of BOMF/MNA system. The experimental results suggest that the effect of silica nanoparticles on fire behavior appears to be related to their dispersion degree.