Research Highlights: The antifungal assay confirmed that knotwood extractives of Scots pine inhibit the growth of wood decay fungi. Heartwood extracts of black locust were found to be much stronger free radical scavengers than the extracts of Scots pine. The extracts were deposited in the lumina and on the wall surface of cells in the impregnated sapwood. Impregnation of the sapwood blocks with Scots pine and black locust extracts reduced the fungal decay of wood. Objectives: Hydrophilic extracts of Scots pine knotwood and black locust heartwood were chemically analyzed, tested for antifungal and antioxidant properties and used for impregnation of beech and Scots pine sapwood. Materials and Methods: Scots pine knotwood and black locust heartwood were extracted, and obtained hydrophilic extractives were chemically analyzed. Extracts were analyzed for antifungal properties with the in vitro well-diffusion method. The free radical scavenging activity of wood extracts was measured colorimetrically. The retention of the extracts in the impregnated sapwood blocks was evaluated with microscopy and gravimetry. A decay test was performed with the mini block test. Results: Almost half of both Scots pine knotwood and black locust heartwood hydrophilic extracts obtained were described by phenolic compounds. The extracts were deposited in the lumina of cells and on the cell wall surface. Extractives of Scots pine knotwood had good inhibitory properties against white- and brown-rot fungi. On the other hand, extractives of black locust heartwood were found to be good radical scavengers, better than knotwood extractives of Scots pine. The extracts of Scots pine knotwood and black locust reduced the fungal decay of the tested sapwood blocks. Conclusions: The results of this research show that the less-valued knotwood of Scots pine and heartwood of black locust are a potential source of antifungal and antioxidant agents for bio-based wood preservatives.

Poly(vinyl alcohol) (PVA) biocomposite films reinforced with cellulose nanofibrils (CNF) and biologically active tannic acid (TA) were prepared. The influence of different concentrations of CNF and TA in the PVA polymer matrix was investigated in terms of mechanical properties, thermal properties and hydrophobicity improvement of the prepared films. The results showed that in all cases the addition of CNF and TA improved the values of tensile strength and elastic modulus. The PVA film with 10 % CNF exhibited a 30 % higher tensile strength, and the three-component PVA film with 2 % CNF and 10 % TA (P2C10T) exhibited a 40 % higher tensile strength compared to the neat PVA film. The thermal properties (T_g, T_onset) of the PVA biocomposite films were greatly improved, with a significant effect observed for the three-component PVA films. The T_g of the PVA film with 10 % CNF and 10 % TA was 87 °C, 12 °C higher than that of the neat PVA film. For three-component PVA biocomposites with 4 % and 6 % CNF and with all weight percentages of TA, the T_onset shifted to a higher temperature range by about 30 °C compared to the neat PVA film. The PVA film with 2 % CNF and 10 % TA exhibited about a 20° higher contact angle than the neat PVA film. Moreover, the addition of both fillers to the PVA matrix resulted in PVA biocomposites with lower water absorption. PVA film with 10 % TA absorbed about 90 % less water and PVA film with 10 % CNF and 10 % TA absorbed about 80 % less water than the neat PVA film after the films were soaked in water for one hour. The better properties of the composite films produced are due to hydrogen and ester bonds between the components of the composite, which was confirmed by FT-IR spectroscopy. Antioxidant effective films were also obtained due to the biologically active TA to the PVA and PVA/CNF systems.

The chemical composition of extractives in the sapwood (SW), heartwood (HW), knotwood (KW), and branchwood (BW of silver fir (Abies alba Mill.) was analyzed, and their antifungal and antioxidant properties were studied. In addition, the variability of extractives content in a centripetal direction, i.e., from the periphery of the stem towards the pith, was investigated. The extracts were analyzed chemically with gravimetry, spectrophotometry, and chromatography. The antifungal and antioxidative properties of the extracts were evaluated by the agar well diffusion method and the diphenyl picrylhydrazyl radical scavenging method. Average amounts of hydrophilic extractives were higher in KW (up to 210.4 mg/g) and BW (148.6 mg/g) than in HW (34.1 mg/g) and SW (14.8 mg/g). Extractives identified included lignans (isolariciresinol, lariciresinol, secoisolariciresinol, pinoresinol, matairesinol) phenolic acids (homovanillic acid, coumaric acid, ferulic acid), and flavonoids epicatechin, taxifolin, quercetin). Secoisolariciresinol was confirmed to be the predominant compound in the KW (29.8 mg/g) and BW (37.6 mg/g) extracts. The largest amount of phenolic compounds was extracted from parts of knots (281.7 mg/g) embedded in the sapwood and from parts of branches (258.9 mg/g) adjacent to the stem. HW contained more lignans in its older sections. Hydrophilic extracts from knots and branches inhibited the growth of wood-decaying fungi and molds. KW and BW extracts were better free radical scavengers than HW extracts. The results of the biological activity tests suggest that the protective function of phenolic extracts in silver fir wood can also be explained by their antioxidative properties. The results of this study describe BW as a potential source of phenolic extractives in silver fir.

Various types of wound-associated wood, such as discoloured wood including knots of living and dead branches, were sampled from common beech trees (Fagus sylvatica L.), extracted, and the extracts have been analysed by GC and colourimetry assay. Sequential pressurised solvent extraction was applied with cyclohexane and aqueous methanol. The yield of hydrophilic compounds was three to five times higher than that of lipophilic extractives. The fractions differed mainly in their hydrophilic moieties. The lipophilic extractives consisted mainly of free fatty acids, fatty alcohols and free sterols. The yield of fatty acids was slightly higher in reaction zones and knots. The content of free sterols was highest in the reaction zones and in the discoloured wood. The hydrophilic extractives consisted of soluble sugars, various acids and phenolic compounds with catechin as the dominant one. Expectedly, the yield of phenolic extractives and catechin (proanthocyanidins) was highest in knots and wound-wood. Discoloured wood gave rise to lower amounts of catechin.