In this study, an experimental investigation was conducted on the mechanical properties of lightweight aggregate concrete (LWAC) with different chopped fibers, including basalt fiber (BF) and polyacrylonitrile fiber (PANF). The LWAC performance was studied in regard to compressive strength, splitting tensile strength and shear strength at age of 28 days. In addition, the oven-dried density and water absorption were measured as well to confirm whether the specimens match the requirement of standard. In total, seven different mixture groups were designed and approximately 104 LWAC samples were tested. The test results showed that the oven-dried densities of the LWAC mixtures were in range of 1.819–1.844 t/m³ which satisfied the definition of LWAC by Chinese Standard. Additionally, water absorption decreased with the increasing of fiber content. The development tendency of the specific strength of LWAC was the same as that of the cube compressive strength. The addition of fibers had a significant effect on reducing water absorption. Adding BF and PANF into concrete had a relatively slight impact on the compressive strength but had an obvious effect on splitting tensile strength, flexural strength and shear strength enhancement, respectively. In that regard, a 1.5% fiber volume fraction of BF and PANF showed the maximum increase in strength. The use of BF and PANF could change the failure morphologies of splitting tensile and flexural destruction but almost had slight impact on the shear failure morphology. The strength enhancement parameter β was proposed to quantify the improvement effect of fibers on cube compressive strength, splitting tensile strength, flexural strength and shear strength, respectively. And the calculation results showed good agreement with test value.

Alkali-activated materials have attracted increasing interest owing to their excellent properties and environmental protection. However, there have been few studies on their creep properties. The aim of this article is to investigate the effect of the stress–strength ratio on the creep property of sodium silicate–based alkali-activated slag (AAS) concrete. For this reason, five groups of AAS concrete with different stress–strength ratios (0.15, 0.3, 0.45, 0.6, and 0.75) were tested. The results indicate that the creep of AAS concrete has a convergent nonlinear stage and a non-convergent stage but not an obvious linear stage. The AAS concrete basically has a consistent creep coefficient and diverse specific creep under a stress–strength ratio of 0.15–0.6. The elasticity modulus of AAS is much smaller than that of ordinary Portland cement (OPC) concrete, which is the reason for the greater creep compared to that in OPC concrete, and the inaccuracy of the model prediction. By applying the actual elastic modulus, the models can predict the specific creep and stress-dependent strain of AAS concrete with a 0.3 stress–strength ratio, except for the B3 model. The secant modulus of AAS concrete decreases linearly with an increase in the stress–strength ratio. Finally, we propose an improved creep model for AAS concrete with a wide stress–strength ratio based on the GL2000 model.

Alkali-activated slag (AAS) is an environmentally friendly green cementitious material that can replace ordinary Portland cement (OPC) and has attracted extensive research by scholars all over the world. However, research regarding its creep performance has been lacking, which in turn affects its further application. The creep of alkali-activated slag concrete is large, and fiber addition has been shown to improve this problem. Polypropylene (PP) fiber has good alkali resistance and is economical. This paper studies the effect of the stress–strength ratio and fiber length on the creep property of PP fiber-reinforced alkali-activated slag (FRAAS) concrete. At the stress–strength ratio of 0.15, PP fiber addition is able to greatly reduce the creep of concrete. When the stress–strength ratio increases, the shorter fiber loses the anchoring force and the holes caused by the longer fiber crack. This in turn leads to the deterioration of the inhibition effect on concrete creep. The CEB-FIP 2010 model is highly accurate, but the final value prediction is small. The early prediction value of the GL2000 model is rather large and conservative. The creep coefficient of the prediction model and the measured secant modulus of PP FRAAS concrete with different fiber lengths under different stress–strength ratios may solve the issue of creep prediction.