In this study, an experimental investigation was conducted on the mechanical properties of lightweight aggregate concrete (LWAC) with different chopped fibers, including basalt fiber (BF) and polyacrylonitrile fiber (PANF). The LWAC performance was studied in regard to compressive strength, splitting tensile strength and shear strength at age of 28 days. In addition, the oven-dried density and water absorption were measured as well to confirm whether the specimens match the requirement of standard. In total, seven different mixture groups were designed and approximately 104 LWAC samples were tested. The test results showed that the oven-dried densities of the LWAC mixtures were in range of 1.819–1.844 t/m³ which satisfied the definition of LWAC by Chinese Standard. Additionally, water absorption decreased with the increasing of fiber content. The development tendency of the specific strength of LWAC was the same as that of the cube compressive strength. The addition of fibers had a significant effect on reducing water absorption. Adding BF and PANF into concrete had a relatively slight impact on the compressive strength but had an obvious effect on splitting tensile strength, flexural strength and shear strength enhancement, respectively. In that regard, a 1.5% fiber volume fraction of BF and PANF showed the maximum increase in strength. The use of BF and PANF could change the failure morphologies of splitting tensile and flexural destruction but almost had slight impact on the shear failure morphology. The strength enhancement parameter β was proposed to quantify the improvement effect of fibers on cube compressive strength, splitting tensile strength, flexural strength and shear strength, respectively. And the calculation results showed good agreement with test value.

With the growth of the global population and the acceleration of industrialization, the problem of water pollution has become increasingly serious, posing a major threat to the ecosystem and human health. Traditional water treatment technologies make it difficult to cope with complex pollution, so the scientific community is actively exploring new and efficient treatment methods. Biochar (BC), as a low-cost, green carbon-based material, exhibits good adsorption and catalytic properties in water treatment due to its porous structure and abundant active functional groups. However, BC’s pure adsorption or catalytic capacity is limited, and researchers have dramatically enhanced its performance through modification means, such as loading metals or heteroatoms. In this paper, we systematically review the recent applications of BC and its modified materials for water treatment in adsorption, Fenton-like, electrocatalytic, photocatalytic, and sonocatalytic systems, and discuss their adsorption/catalytic mechanisms. However, most of the research in this field is at the laboratory simulation stage and still needs much improvement before it can be applied in large-scale wastewater treatment. This review improves the understanding of the pollutant adsorption/catalytic properties and mechanisms of BC-based materials, analyzes the limitations of the current studies, and investigates future directions.

Alkali-activated materials have attracted increasing interest owing to their excellent properties and environmental protection. However, there have been few studies on their creep properties. The aim of this article is to investigate the effect of the stress–strength ratio on the creep property of sodium silicate–based alkali-activated slag (AAS) concrete. For this reason, five groups of AAS concrete with different stress–strength ratios (0.15, 0.3, 0.45, 0.6, and 0.75) were tested. The results indicate that the creep of AAS concrete has a convergent nonlinear stage and a non-convergent stage but not an obvious linear stage. The AAS concrete basically has a consistent creep coefficient and diverse specific creep under a stress–strength ratio of 0.15–0.6. The elasticity modulus of AAS is much smaller than that of ordinary Portland cement (OPC) concrete, which is the reason for the greater creep compared to that in OPC concrete, and the inaccuracy of the model prediction. By applying the actual elastic modulus, the models can predict the specific creep and stress-dependent strain of AAS concrete with a 0.3 stress–strength ratio, except for the B3 model. The secant modulus of AAS concrete decreases linearly with an increase in the stress–strength ratio. Finally, we propose an improved creep model for AAS concrete with a wide stress–strength ratio based on the GL2000 model.