During femtosecond laser fabrication, photons are mainly absorbed by electrons, and the subsequent energy transfer from electrons to ions is of picosecond order. Hence, lattice motion is negligible within the femtosecond pulse duration, whereas femtosecond photon-electron interactions dominate the entire fabrication process. Therefore, femtosecond laser fabrication must be improved by controlling localized transient electron dynamics, which poses a challenge for measuring and controlling at the electron level during fabrication processes. Pump-probe spectroscopy presents a viable solution, which can be used to observe electron dynamics during a chemical reaction. In fact, femtosecond pulse durations are shorter than many physical/chemical characteristic times, which permits manipulating, adjusting, or interfering with electron dynamics. Hence, we proposed to control localized transient electron dynamics by temporally or spatially shaping femtosecond pulses, and further to modify localized transient materials properties, and then to adjust material phase change, and eventually to implement a novel fabrication method. This review covers our progresses over the past decade regarding electrons dynamics control (EDC) by shaping femtosecond laser pulses in micro/nanomanufacturing: (1) Theoretical models were developed to prove EDC feasibility and reveal its mechanisms; (2) on the basis of the theoretical predictions, many experiments are conducted to validate our EDC-based femtosecond laser fabrication method. Seven examples are reported, which proves that the proposed method can significantly improve fabrication precision, quality, throughput and repeatability and effectively control micro/nanoscale structures; (3) a multiscale measurement system was proposed and developed to study the fundamentals of EDC from the femtosecond scale to the nanosecond scale and to the millisecond scale; and (4) As an example of practical applications, our method was employed to fabricate some key structures in one of the 16 Chinese National S&T Major Projects, for which electron dynamics were measured using our multiscale measurement system.

This paper presents an investigation on the humidity sensitivity of deposited multi-walled carbon nanotube (MWCNT) networks using ac dielectrophoresis (DEP) between interdigitated electrodes (IDEs). MWCNTs dispersed in ethanol were trapped and enriched between IDEs on a Si/SiO₂ substrate under a positive DEP force. After the DEP process, the ethanol was evaporated and the MWCNT network on a substrate with IDEs was put into a furnace for repeated thermal annealing. It was found that the resistance stability of the network was effectively improved through thermal annealing. The humidity sensitivity was obtained by measuring the resistance of the MWCNT network with different relative humidity at room temperature. The experimental results show the resistance increases linearly with increasing the relative humidity from 25% to 95% RH with a sensitivity of 0.5%/%RH. The MWCNT networks have a reversible humidity sensing capacity with response time and recovery time of about 3 s and 25 s, respectively. The resistance is dependent on temperature with a negative coefficient of about -0.33%/K in a temperature range from 293 K to 393 K.