This study investigated several approaches for silane-removal from the surface of short carbon fiber bundles, and short carbon fibers uniformly dispersed in cement to produce a novel compound of carbon-fiber-reinforced cement. In order to facilitate the uniform distribution of short carbon fibers in the carbon-fiber-reinforced cement, it is necessary to remove the silane from the carbon fiber’s surface. Short carbon fiber bundles were submerged into a pure water, sodium hydroxide solution, and acetic acid solution, and placed in high-temperature furnace used to remove silane from the carbon fiber surface. The results were observed under a scanning electron microscope to determine the level of silane removal from the surface, and an effective method for removing the silane was developed from among the several approaches. This method employed a pneumatic dispersion device to disperse carbon fibers then mixed in a high-early-strength cement which led to an excellent compressive and impact-resistance performance of carbon-fiber-reinforced cement. Final testing showed that the compressive strength and impact energy increased by 14.1% and 145%, respectively.

In this paper, a strengthening method for the damaged high-temperature steel pipeline using inorganic insulation material which was confined by carbon fiber reinforcement plastic (CFRP) composite materials was proposed. Two inorganic insulation materials were composed of magnesium phosphate cement (MPC) mixing with perlite and vermiculite powders, respectively. The influences of insulation material composites with various ratios of the perlite or vermiculite powder were discussed, in terms of compressive strength and thermal conductivity coefficients of inorganic insulation materials. The insulation materials confined by carbon fiber reinforced polymer jackets for enhancing the mechanical behavior were also investigated. From the experimental results, the main finding of the work was that the inorganic insulation materials added to the perlite powder represented greater insulation capability than added vermiculite ones under the condition of the same compressive strength. Different ratios of perlite inorganic insulation material cylinders with the dimension of ϕ 10 cm × 20 cm were confined by one layer and two layers of CFRP composite material. The compressive strength of the specimens increased by 258%–927% after using 1-layer CFRP composite material and increased by 480%–1541% after applying 2-layer CFRP composite material. A peak strength prediction model of insulation materials confined by CFRP was proposed, and it was found that the proposed model accurately predicted the peak strength of the inorganic insulation material cylinder. Finally, a verification test of the strengthening method for damaged high-temperature pipeline was performed to prove that the proposed strengthening method is feasible.

In this study, two different compositions of submicron-structured titanium (760 nm) and micron-structured chromium (4.66 μm) powders were mixed to fabricate Cr-31.2 mass% Ti alloys by vacuum hot-press sintering. The research imposed various hot-press sintering pressures (20, 35 and 50 MPa), while the sintering temperature maintained at 1250°C for 1 h. The experimental results showed that the optimum parameters of the hot-press sintered Cr-31.2 mass% Ti alloys were 1250°C at 50 MPa for 1 h. Also, the relative density reached 99.94%, the closed porosity decreased to 0.04% and the hardness and transverse rupture strength (TRS) values increased to 81.90 HRA and 448.53 MPa, respectively. Moreover, the electrical conductivity is enhanced to 1.58 × 104 S·cm–1. However, the grain growth generated during the high-temperature and high-pressure of the hot-press sintering process resulted in the grain coarsening phenomenon of the Cr-31.2 mass% Ti alloys after 1250°C hot-press sintering at 50 MPa for 1 h. In addition, the Cr-31.2 mass% Ti alloys were fabricated with the submicron-structured titanium (760 nm) and chromium (588 nm) powders showed more effective compaction than the micron-structured titanium (760 nm) and chromium (4.66 μm) powders did. The closed porosity decreases to 0.02% and the hardness values increase to 83.23 HRA. However, the agglomeration phenomenon of the Cr phase and brittleness of the TiCr2 Laves phases easily led to a slight decrease in TRS (400.54 MPa).

This study developed 3D-printable cement mortar (3DPCM) incorporating modified basic oxygen furnace slag (MBOFS) sand and waste printed circuit board powder (WPCBP). Five WPCBP-to-cement ratios, namely 0, 10, 20, 30, and 40 wt.%, were adopted, and the printability of each mixture was first evaluated. Subsequently, the compressive, flexural, and splitting tensile behaviors of mold-cast and 3D-printed specimens were compared, and the structural response of 3D-printed truss members was assessed through four-point bending tests and finite element analysis. The results showed that all mixtures could be printed stably. For the standard 3D-printed specimens, WPCBP/C = 20 wt.% provided the highest quasi-static mechanical performance, and the mechanical response exhibited clear anisotropic behavior. In contrast, the mechanical performance of the mold-cast specimens decreased with increasing WPCBP content. In the 3D-printed truss members, the average peak load increased from 8.041 to 20.710 kN, the displacement corresponding to the peak load increased from 0.201 to 0.683 mm, and the finite element analysis reasonably captured the overall load–displacement response. Overall, MBOFS sand and WPCBP can be effectively incorporated into 3DPCM and show potential for sustainable structural material applications.