Composite materials that combine the unique properties of zeolitic imidazolate frameworks (ZIFs) and carbon nanotubes (CNTs) can give rise to novel applications. Here, ZIF-8/CNT composites were successfully prepared with and without the addition of an agent template. The size of the ZIF-8 crystals in the composite materials was controlled by varying the template, feeding order, and concentration of reactants. Thus, ZIF-8 crystals with a wide variety of sizes (from nano- to micrometer size, which is range that differs by a factor of 10) were obtained, depending on the conditions. This size-controllable synthesis of ZIF-8 was achieved by modifying the number of nucleation sites on the CNTs, as revealed by density functional theory (DFT) calculations. This work provides an efficient method for preparing ZIF-8/CNT composites with controllable size and can pave the way for the synthesis of other metal-organic framework (MOF)/CNT composite materials.

A facile and practical heterogeneous copper nanoparticles catalyst ([email protected]) was prepared by the incorporation of Cu(OAc)₂ to amide and ether functionalized porous organic polymers (AEPOP) that were efficiently prepared by condensation of 4,4′-diaminodiphenyl ether with 1,3,5-benzenetricarbonyl chloride. The prepared AEPOP and [email protected] were characterized by SEM, BET, TEM, ICP, FT-IR and XRD. With TBHP (70 wt% in water) as oxidant and solvent, [email protected] showed excellent catalytic activity for the selective oxidation of benzylic C–H bonds. Among the oxidation of alkyl benzenes to ketones, secondary alcohols to ketones, and primary alcohols to acids, the copper catalyst exhibited remarkable selectivity and reactivity for a broad range of substrates in excellent yields. Furthermore, the experimental operation was very facile and the heterogeneous catalyst could be easily recovered by filtration separation.