Color match and water sorption are two factors that affect restorative materials. Discoloration is essential in the lifespan of restorations. The aim of this study was to evaluate color change and water sorption of nine flowable composites at multiple time points over 6 months. 60 samples of each composite were divided into two groups (Color Change and Water Sorption/Solubility). Each Color Change group was divided into six subgroups, which were immersed in distilled water (DW), coffee (CF), Coca-Cola (CC), red wine (RW), tea (TE) and orange juice (OJ). The color was measured at the baseline, 1, 2, 3 and 4 weeks, and 3 and 6 months and color change values (ΔE) were calculated. Each Water Sorption [W_S]/Solubility [W_L] group was tested according to ISO 4049:2009. The data were evaluated using two-way ANOVA, Fisher’s post-hoc test and Pearson’s correlation test. The composite with the lowest ΔE differed for each solution: Filtek™ Bulk Fill in DW (∆E = 0.73 (0.17–1.759)); Vertise Flow in CF (∆E = 14.75 (7.91–27.41)), in TE (∆E = 7.27 (2.81–24.81)) and OJ (∆E = 3.17 (0.87–9.92)); Tetric EvoFlow® in CC (∆E = 1.27 (0.45–4.02)); and Filtek™ Supreme XTE in RW (∆E = 8.88 (5.23–19.59)). RW caused the most discoloration (∆E = 23.62 (4.93–51.36)). Vertise Flow showed the highest water sorption (W_S = 69.10 ± 7.19). The Pearson test showed statistically significant positive correlations between water sorption and solubility and between water sorption and ∆E; the positive solubility-∆E correlation was not statistically significant. The findings suggest that water sorption is one factor associated with the ability of composites to discolor; however, discoloration is a multifactorial problem.

The aim of this study was to perform a narrative review to identify the modifications applied to the chemical structure of third- and fourth-generation zirconia ceramics and to determine the influence of these changes on the mechanical and optical properties. A bibliographical search using relevant keywords was conducted in the PubMed^® and EBSCO databases. The abstracts and full texts of the resulting articles were reviewed for final inclusion. Fifty-four articles were included in this review. The analyzed topics were: (1) the composition of first- and second-generation zirconia materials (Y-TZP), (2) the behavior of the studied generations in relation to mechanical and optical properties, and (3) the modifications that were carried out on third-generation (5Y-TZP) and fourth-generation (4Y-TZP) zirconia materials. However, studies focusing on these specific characteristics in third- and fourth-generation zirconia materials are scarce. The review shows that there is a lack of sufficient knowledge about the chemical modifications of zirconia in the new generations.

Education currently focuses on improving academic knowledge and clinical skills, but it is also important for students to develop personal and interpersonal skills from the start of their clinical practice. The aim was to evaluate the effect of peer mentoring in third-year students and to gauge the evolution of non-technical skills (NTS) acquisition up to the fifth year. The study groups were selected between September 2015 and May 2018, based on the NTS training they had or had not received: (1) fifth-year students with no training (G1); (2) third-year students mentored in NTS (G2a); and (3) a small group of fifth-year students who became mentors (G2b). A total of 276 students who took part in this study were assessed using a 114-item self-evaluation questionnaire. Data were collected from seven surveys conducted between September 2015 and May 2018, and statistical analysis was performed using one-way ANOVA and Fisher’s post-hoc test. G2a improved their non-technical skill acquisition over three years of clinical training up to their fifth year. This group and G2b showed statistically significant differences compared to non-mentored students (G1). Peer mentoring at the beginning of clinical practice is a valid option for training students in non-technical skills.

Bioactive materials have emerged as a promising alternative to conventional restorative materials as part of more conservative dentistry. The aim of this study was to evaluate and compare the shear bond strength (SBS) and microleakage of a new bioactive restorative material, two bulk-fill restorative composites, and a conventional composite at 24 h, 4 weeks, and 8 weeks. Three hundred and sixty molars and premolars were divided into four groups: ACTIVA™ BioACTIVE Restorative™, Filtek™ Bulk-Fill Restorative Composite, Tetric^® N-Ceram Bulk-Fill Composite, and G-aenial^® Composite. The normality of the data was determined with the Kolmogorov-Smirnov test, then the two-way ANOVA and Fisher’s test were used for analyzing SBS data, and the Kruskal-Wallis and DSCF tests were conducted to analyze the microleakage. In the SBS test, there were no statistically significant differences between materials (p = 0.587), and the relation between material and time (p = 0.467), time points showed statistically significant differences (p = 0.016). As for the microleakage, statistically significant differences were found for all three time periods (p < 0.05), showing the conventional composite to have the lowest microleakage, followed by the bioactive material, and lastly the two bulk-fill composites. In conclusion, the new bioactive material has similar evaluated properties to bulk-fill composites (bond strength) and conventional composites (bond strength and microleakage) and can be used as an alternative restorative material.

Ion release from dental implants and prosthetic restoration can affect osteointegration and implant viability over a long period of time. Therefore, the aim of this study was to study the ion release from implants and crowns, with and without intermediate anodized abutments, in two different media, simulating clinical conditions. The implants, intermediate prosthetic abutments and Cr–Co crowns were divided into two groups depending on the media: Hanks’ solution and 1% lactic acid, simulating body fluids and microbiologically conditioned fluids, respectively. The study followed the ISO 10271:2011 and 10993-15:2000 standards modified to simulate the replacement of fluids in the oral environment. The ions’ release was measured by inductively coupled plasma mass spectroscopy (ICP-EOS), and only aluminum, chromium, cobalt, titanium and vanadium were identified. Ion concentration was higher in lactic acid than in Hanks’ solution at all time points (p < 0.05). Only vanadium showed a very low ion release in lactic acid, with no statistically significant differences from the ion release in Hanks’ solution (p = 0.524). Both anodized abutments and the immersion medium influenced the release of ions and affected the corrosion of these structures. The presence of an intermediate anodized abutment also affected ion release, as the level of ions was lower in groups with this component.

Biodentine^® is a bioactive dentin coating widely used for dental restoration; however, its adhesion to the substrate could limit its clinical success. The aim of this study was to evaluate the shear bond strength (SBS) between Biodentine^® and a composite resin, using different types of adhesive. In total, 120 acrylic blocks with a central hole were prepared. They were fully filled with Biodentine^®, and divided into two time groups: 12 min (n = 60) and 24 h (n = 60); each group was subdivided into four groups according to the adhesive: three-step etch and rinse (3-E&R) (n = 15), two-step etch and rinse (n = 15), and a universal adhesive subdivided into two groups, two-step etch and rinse (n = 15) and one-step self-etch adhesive system (n = 15). After adhesive application, the composite was applied and stored at 100% humidity, at 37 °C, for 24 h, before the SBS test. Data were analyzed with one-way ANOVA, Fisher post hoc test, and Kolmogorov–Smirnov test. The 12-min group showed statistically significant differences (p = 0.009), with the highest values of adhesion for 3-E&R. No statistically significant differences were observed for the 24-h group (p = 0.813) and between adhesive systems (p = 0.071) regardless of adhesion time. Higher adhesion values were found at 24 h. It is essential to consider the longest setting time for Biodentine^®. In terms of adhesive, 3-E&R had the highest adhesion values.