Since the discovery of buckminsterfullerene over 30 years ago, sp²-hybridised carbon nanomaterials (including fullerenes, carbon nanotubes, and graphene) have stimulated new science and technology across a huge range of fields. Despite the impressive intrinsic properties, challenges in processing and chemical modification continue to hinder applications. Charged carbon nanomaterials (CCNs), formed via the reduction or oxidation of these carbon nanomaterials, facilitate dissolution, purification, separation, chemical modification, and assembly. This approach provides a compelling alternative to traditional damaging and restrictive liquid phase exfoliation routes. The broad chemistry of CCNs not only provides a versatile and potent means to modify the properties of the parent nanomaterial but also raises interesting scientific issues. This review focuses on the fundamental structural forms: buckminsterfullerene, single-walled carbon nanotubes, and single-layer graphene, describing the generation of their respective charged nanocarbon species, their interactions with solvents, chemical reactivity, specific (opto)electronic properties, and emerging applications.

Mechanical properties of rod-like cellulose nanocrystals (CNCs) offer great potential as bioderived reinforcement in (nano)composites. Polyvinyl alcohol (PVOH) is a useful industrial material and very compatible with CNC chemistry. High performance CNC/PVOH composite fibers were produced coaxial coagulation spinning, followed by hot-drawing. DSC and WAXS showed that CNCs increase the alignment and crystallinity of PVOH, as well as providing direct reinforcement, leading to enhanced fiber strength and stiffness. At 40 wt.% CNC loading, the strength and stiffness reached 880 MPa and 29.9 GPa, exceeding the properties of most other nanocellulose based composite fibers previously reported.

Graphene nanoplatelets (GNP) were exfoliated using a nondestructive chemical reduction method and subsequently decorated with polymers using two different approaches: grafting from and grafting to. Poly(methyl methacrylate) (PMMA) with varying molecular weights was covalently attached to the GNP layers using both methods. The grafting ratios were higher (44.6% to 126.5%) for the grafting from approach compared to the grafting to approach (12.6% to 20.3%). The products were characterized using thermogravimetric analysis–mass spectrometry (TGA-MS), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), atomic force microscopy (AFM), and transmission electron microscopy (TEM). The grafting from products showed an increase in the grafting ratio and dispersibility in acetone with increasing monomer supply; on the other hand, due to steric effects, the grafting to products showed lower absolute grafting ratios and a decreasing trend with increasing polymer molecular weight. The excellent dispersibility of the grafting from functionalized graphene, 900 μg/mL in acetone, indicates an increased compatibility with the solvent and the potential to increase graphene reinforcement performance in nanocomposite applications.

High torsional strength fibers are of practical interest for applications such as artificial muscles, electric generators, and actuators. Herein, we maximize torsional strength by understanding, measuring, and overcoming rheological thresholds of nanocarbon (nanotube/graphene oxide) dopes. The formed fibers show enhanced structure across multiple length scales, modified hierarchy, and improved mechanical properties. In particular, the torsional properties were examined, with high shear strength (914 MPa) attributed to nanotubes but magnified by their structure, intercalating graphene sheets. This design approach has the potential to realize the hierarchical dimensional hybrids, and may also be useful to build the effective network structure of heterogeneous materials.