This paper deals with the “modern” plaster mortars based on air lime, hydraulic lime, and cement used between the 1950s and 1990s of the last century, taking, as a case study, a historical building of the Cagliari city whose foundations and ground floor are cut into in-situ limestone. Different plaster layers (i.e., arriccio and intonachino, paint), applied on the excavated limestone walls, were collected from cave-room. All samples were analysed by optical and electron (SEM-EDS) microscopy and X-ray diffractometry (XRD) in order to define their microstructures, textures and compositional features. In addition, real and bulk density, water and helium open porosity, water absorption kinetic, and saturation index were measured. By microscopic imaging analyses, the binder/aggregate ratio as vol.% was determined. Results revealed that cement mortars, composed mainly of C-S-H, C-A-H, and C-F-H phases, given their high hydraulicity, low open porosity, and a rigid behaviour, showed a good chemical but not physical–mechanical adherence, as they were often found detached from the substrate and frequently loaded with salt efflorescence. On the contrary, the hydraulic lime-based mortars, characterised by a binder composed of C-S-H and C-A-H phases and calcite derived from the portlandite carbonation, showed a greater affinity with limestone substrate and other plasters. Thus, they are more suitable to be used as a repair mortar, showing a long durability on the time. The thin air lime-based plasters (intonachino) showed a good adhesion to the substrate, exerting their coating function better than the harder, cement-based mortars. Lime-based wall paints have a good chemical adhesion and adaptability to the irregular surface of the substrate, due to low thickness of lime paint layers (<1 mm) that confers an elastic physical behaviour.

The topic of this study is the archaeometric characterization of mortars from Villa del Pezzolo, a Roman Villa located in Seiano (Napoli-Campania, Italy), dated between the 1st century B.C. and the 3rd century A.D. Mortars were analyzed by means of a multi-analytical approach (polarized optical microscopy, X-ray powder diffraction, scanning electron microscopy and energy-dispersed spectrometry, thermal analyses and mercury intrusion porosimetry) according to existing recommendations. Analytical results evidenced the use of local geomaterials composed of sedimentary and volcanic aggregates in the mix design and confirmed the three distinct building phases identified by archaeologists. Volcanic tuff fragments, identified in the 1st building phase can be ascribed to Campanian Ignimbrite formation, widely cropping out in the Sorrento Peninsula, as confirmed by the presence of glassy shards, partially devitrified and replaced by authigenic feldspar, a typical feature of welded grey ignimbrite lithofacies (WGI). Volcanic aggregates in samples of the 2nd and 3rd building phases show, instead, the presence of leucite-bearing volcanic scoriae and garnet crystal fragments related to Somma-Vesuvius products. Study of these mortars allowed us to: (1) understand the production technologies; (2) highlight use of materials with hydraulic behavior, such as volcanic and fictile fragments; (3) confirm the three building phases from compositional features of mortars and (4) highlight the change over time of the volcanic aggregate for mortars mix-design.