The main challenge in the production of metal matrix composites reinforced by carbon nanotubes (CNTs) is the development of a manufacturing process ensuring the dispersion of nanoparticles without damaging them, and the formation of a strong bond with the metallic matrix to achieve an effective load transfer, so that the maximum reinforcement effect of CNTs will be accomplished. This research focuses on the production by powder metallurgy of aluminum and nickel matrix composites reinforced by CNTs, using ultrasonication as the dispersion and mixture process. Microstructural characterization of nanocomposites was performed by optical microscopy (OM), scanning and transmission electron microscopy (SEM and TEM), electron backscattered diffraction (EBSD) and high-resolution transmission electron microscopy (HRTEM). Microstructural characterization revealed that the use of ultrasonication as the dispersion and mixture process in the production of Al/CNT and Ni/CNT nanocomposites promoted the dispersion and embedding of individual CNT in the metallic matrices. CNT clusters at grain boundary junctions were also observed. The strengthening effect of the CNTs is shown by the increase in hardness for all nanocomposites. The highest hardness values were observed for Al/CNT and Ni/CNT nanocomposites, with a 1.00 vol % CNTs.

The use of lignocellulosic remnants of the açaí agro-business will benefit the environment with a precursor material for biomedical applications. Nanocellulose (NC) allows the biomimetic growth of biphasic ceramics on its surface, with characteristics compatible with bone tissue, including bioactive properties and biocompatibility. In this study, the composites were obtained from açaí tegument (Euterpe Oleracea Mart.) NC using acid hydrolysis. The characterization performed by scanning electron microscopy showed the characteristic crystals of hydroxyapatite (HA) and calcium triphosphate (β-TCP) based on the results of X-ray diffraction, with the peak at 22°, showing the NC nucleation of HA and peak at 17° showing tricalcium phosphate (β-TCP). Fourier transform infrared spectroscopy confirmed the presence of O-H at 3400 cm⁻¹ and C-H at 2900 cm⁻¹, which is characteristic of cellulose; peaks were also observed at 1609 cm⁻¹, verifying the reduction in lignin content. Groups PO₄⁻³ at approximately 1070 cm⁻¹, P-OH at 910–1040 cm⁻¹, and HCO₃⁻ at 2450 cm⁻¹ confirmed the formation of HA and β-TCP. The zeta potential had a range of −11 ± 23.8 mV related to particle size, which had a range of 164.2 × 10⁻⁹–4748 × 10⁻⁹ m.

Natural lignocellulosic fibers (NLFs) have in recent decades appeared as sustainable reinforcement alternatives to replace synthetic fibers in polymer composite material applications. In this work, for the first time, the periquiteira (Cochlospermum orinocense), a lesser known NLF from the Amazon region, was analyzed for its density and, by X-ray diffraction (XRD), to calculate the crystallinity index as well as the microfibrillar angle (MFA), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), scanning electron analysis (SEM) and tensile strength. The apparent density found for the periquiteira fiber was 0.43 g/cm³, one of the NLF’s lowest. XRD analysis indicated a crystallinity index of 70.49% and MFA of 7.32°. The TGA disclosed thermal stability up to 250 °C. The FTIR analysis indicated the presence of functional groups characteristic of NLFs. The SEM morphological analysis revealed that the periquiteira fiber presents fine bundles of fibrils and a rough surface throughout its entire length. The average strength value of the periquiteira fiber was found as 178 MPa. These preliminary results indicate that the periquiteira fiber has the potential to be used as a reinforcing agent in polymeric matrices and can generate a lightweight composite with excellent mechanical properties that can be used in various industrial sectors.