Microstructured optical fibers (MOFs) are traditionally prepared using the stack and draw technique. In order to avoid the interfaces problems observed in chalcogenide glasses, we have developed a new casting method to prepare the chalcogenide preform. This method allows to reach optical losses around 0.4 dB/m at 1.55 µm and less than 0.05 dB/m in the mid IR. Various As₃₈Se₆₂ chalcogenide microstructured fibers have been prepared in order to combine large non linear index of these glasses with the mode control offered by MOF structures. Small core fibers have been drawn to enhance the non linearities. In one of these, three Stokes order have been generated by Raman scattering in a suspended core MOF pumped at 1995 nm.

Applications involving optical fibers have grown considerably in recent years with intense levels of research having been focused on the development of not only new generations of optical fiber materials and designs, but also on new processes for their preparation. In this paper, we review the latest developments in advanced materials for optical fibers ranging from silica, to semi-conductors, to particle-containing glasses, to chalcogenides and also in process-related innovations.

We report the fabrication of a microstructured optical fiber drawn from a soft glass 3D printed preform. For this proof of concept, a chalcogenide glass that is well known for its capability to be shaped at low temperature and its mid-infrared transmission was selected: Te₂₀As₃₀Se₅₀. The obtained negative curvature hollow core fiber shows several transmission bands in the 2–12 µm range that are reproduced numerically using finite element-based simulations and coupled mode theory.

Optics InfoBase is the Optical Society's online library for flagship journals, partnered and copublished journals, and recent proceedings from OSA conferences.

The realization of an all-solid microstructured optical fiber based on chalcogenide glasses was achieved. The fiber presents As₂S₃ inclusions selected as low refractive index material (n = 2.4) embedded in a As₃₈Se₆₂ glass matrix (n = 2.8). The single mode regime of the fiber was demonstrated both theoretically by multipole method calculations and experimentally by near field measurements. Optical transmission measurements of the microstructured fiber and single index fibers made of the initial glasses reveal an excess of losses as high as 6-7 dB/m. This excess is not due to the guide geometry but can be explained by the presence of defects in the glass interface regions.

A highly birefringent polarization-maintaining chalcogenide microstructured optical fiber (MOF) covering the 3-8.5 µm wavelength range has been realized for the first time. The fiber cross-section consists of 3 rings of circular air holes with 2 larger holes adjacent to the core. Birefringence properties are calculated by using the vector finite-element method and are compared to the experimental ones. The group birefringence is 1.5x10⁻³ and fiber losses are equal to 0.8 dB/m at 7.55 µm.