In this work, we experimentally investigated the solidification behavior of functionalized graphene-based phase change nanocomposites inside a sphere. The influence of graphene nanoplatelets on thermal transport and rheological characteristics of the such nanocomposites were also discussed. We adopted the covalent functionalization method to prepare highly stable phase change nanocomposites using commercially available phase change material (PCM) OM08 as the host matrix and graphene nanoplatelets (GnPs) with 0.1, 0.3, and 0.5 volume percentage as the nano inclusions. We report a maximum thermal conductivity enhancement of ~102 and ~46% with 0.5 vol% in the solid and liquid states, respectively. Rheological measurements show that the pure PCM shows Newtonian behavior, whereas the inclusion of GnPs leads to the transition to non-Newtonian behavior, especially at lower shear rates. Viscosity of the nanocomposite increases with an increase in the volume fraction of GnP. For 0.5 vol% of GnPs, maximum increase in viscosity was found to be ~37% at a shear rate of 1000 s⁻¹. Time required for complete solidification decreases with the loading of GnPs. Maximum reduction in solidification time with 0.5 vol% of GnPs was ~40% for bath temperature of −10°C.

In the present work, the freezing and melting characteristics of water seeded with chemically functionalized graphene nanoplatelets in a vertical cylindrical capsule were experimentally studied. The volume percentage of functionalized graphene nanoplatelets varied from 0.1% to 0.5% with an interval of 0.1%. The stability of the synthesized samples was measured using zeta potential analyzer. The thermal conductivity of the nanocomposite samples was experimentally measured using the transient hot wire method. A ~24% (maximum) increase in the thermal conductivity was observed for the 0.5% volume percentage in the liquid state, while a ~53% enhancement was observed in the solid state. The freezing and melting behavior of water dispersed with graphene nanoplatelets was assessed using a cylindrical stainless steel capsule in a constant temperature bath. The bath temperatures considered for studying the freezing characteristics were −6 °C and −10 °C, while to study the melting characteristics the bath temperature was set as 31 °C and 36 °C. The freezing and melting time decreased for all the test conditions when the volume percentage of GnP increased. The freezing rate was enhanced by ~43% and ~32% for the bath temperatures of −6 °C and −10 °C, respectively, at 0.5 vol % of graphene loading. The melting rate was enhanced by ~42% and ~63% for the bath temperatures of 31 °C and 36 °C, respectively, at 0.5 vol % of graphene loading.