This paper presents a literature review concerning the characteristics of MgO (magnesium oxide or magnesia) and its application in cementitious materials. It starts with the characterization of MgO in terms of production processes, calcination temperatures, reactivity, and physical properties. Relationships between different MgO characteristics are established. Then, the influence of MgO incorporation on the properties of cementitious materials is investigated. The mechanical strength and durability behaviour of cement pastes, mortars and concrete mixes made with MgO are discussed. The studied properties of MgO–cement mixes include compressive strength, flexural strength, tensile strength, modulus of elasticity, water absorption, porosity, carbonation, chloride ion penetration, shrinkage, expansion, and hydration degree. In addition, microscopic analyses of MgO-cement mixes are also assessed. Summarizing the results of different studies, it is concluded that MgO incorporation in cementitious materials generally decreases the mechanical strength and shrinkage, and increases the porosity, expansion, carbonation and chloride ion migration. However, it should be emphasized that the properties of the specific MgO used (mainly the calcination temperature, the reactivity and the surface area) have a significant influence on the characteristics of the cementitious materials produced.

For the efficient and durable design of concrete, the role of fiber-reinforcements with mineral admixtures needs to be properly investigated considering various factors such as contents of fibers and potential supplementary cementitious material. Interactive effects of fibers and mineral admixtures are also needed to be appropriately studied. In this paper, properties of concrete were investigated with individual and combined incorporation of steel fiber (SF) and micro-silica (MS). SF was used at six different levels i.e., low fiber volume (0.05% and 0.1%), medium fiber volume (0.25% and 0.5%) and high fiber volume (1% and 2%). Each volume fraction of SF was investigated with 0%, 5% and 10% MS as by volume of binder. All concrete mixtures were assessed based on the results of important mechanical and permeability tests. The results revealed that varying fiber dosage showed mixed effects on the compressive (compressive strength and elastic modulus) and permeability (water absorption and chloride ion penetration) properties of concrete. Generally, low to medium volume fractions of fibers were useful in advancing the compressive strength and elastic modulus of concrete, whereas high fiber fractions showed detrimental effects on compressive strength and permeability resistance. The addition of MS with SF is not only beneficial to boost the strength properties, but it also improves the interaction between fibers and binder matrix. MS minimizes the negative effects of high fiber doses on the properties of concrete.

The mechanical behavior and transport properties of cement pastes reinforced with various types and amounts of pristine and functionalized carbon nanotubes (CNTs) are characterized for different water to cement (w/c) ratios. The flexural strength, compressive strength, and dynamic modulus of elasticity of CNT-reinforced cement pastes were up to 38%, 58%, and 22% higher than those of unreinforced pastes, respectively. CNTs were also effective in decreasing the drying shrinkage of cement pastes to 87% lower than that of reference pastes at early ages. Water absorption by immersion and capillary absorption could be also reduced as much as 16% and 38%, respectively. Microstructure and thermogravimetric analysis evidenced effective dispersion, microcrack bridging, and nucleation effects of CNT-reinforced cement matrices. Results show that depending on the type and dispersion procedure, CNTs effectively contribute for the reinforcement of cementitious materials, regardless of w/c ratio.

Portland cement concrete is fragile in tension and it has numerous negative impacts on the environment. To deal with these issues, both fiber reinforcement and recycled materials can be utilized to manufacture sustainable and ductile concrete. In this study, the synergistic effects of high-performance mineral admixture silica fume and glass fiber reinforcement were investigated on the hardened properties of RC. For this purpose, two concrete mix families, namely, NC and RC were prepared. To understand the benefits of synergistic utilization of glass fiber and silica fume, in both NC and RC, 0.5% glass fiber was incorporated with three different levels of silica fume. i.e., 0%, 5%, and 10%. Both strength and permeability-related durability properties were investigated. Results revealed that combined incorporation of 0.5% fiber and 10% silica fume can help in the production of RC having better mechanical and durability performance compared to reference “NC”. Simultaneous incorporation of silica fume and glass fiber produces a combined effect greater than their individual effects on both mechanical and permeability properties of concrete. Silica fume plays a very dominant and positive role in the development of CS, WA, and CIPR of RC, whereas glass fiber plays a vital role in upgrading STS and FS of RC and whereas, with the addition of 0.5% glass fiber, RC can yield 8–9 times higher flexural toughness than that of the plain NC.

This study applies a methodology to evaluate the ecotoxicological potential of raw materials and cement-based construction materials. In this study, natural aggregates and Portland cement were replaced with non-conventional recycled concrete aggregates (RA) and fly ash (FA), respectively, in the production of two concrete products alternative to conventional concrete (used as reference). The experimental program involved assessing both the chemical properties (non-metallic and metallic parameters) and ecotoxicity data (battery of tests with the luminescent bacterium Vibrio fischeri, the freshwater crustacean Daphnia magna, and the yeast Saccharomyces cerevisiae) of eluates obtained from leaching tests of RA, FA, and the three concrete mixes. Even though the results indicated that RA and FA have the ability to release some chemicals into the water and induce its alkalinisation, the respective eluate samples presented no or low levels of potential ecotoxicity. However, eluates from concrete mixes produced with a replacement ratio of Portland cement with 60% of FA and 100% of natural aggregates and produced with 60% of FA and 100% of RA were classified as clearly ecotoxic mainly towards Daphnia magna mobility. Therefore, raw materials with weak evidences of ecotoxicity could lead to the production of concrete products with high ecotoxicological potential. Overall, the results obtained highlight the importance of integrating data from the chemical and ecotoxicological characterization of materials’ eluate samples aiming to assess the possible environmental risk of the construction materials, namely of incorporating non-conventional raw materials in concrete, and contributing to achieve construction sustainability.