The use of natural fibers as reinforcement in polymer composites has been a focus of interest. However, these composites exhibit lower mechanical properties than those of pure polymers because of the low interfacial interactions between the hydrophobic polymer matrix and the hydrophilic fiber. To overcome this problem, different chemical treatments applied to the fibers have been reported. One of the most used treatments is mercerization, which can improve adhesion between the fiber and polymeric matrix. Another chemical treatment involves the use of acids (stearic and oleic acids). The chemically treated fibers used in composite materials showed improved mechanical properties

The present study reports the results of rheological behavior of renewable composites, based on a matrix of high density polyethylene (HDPE), made from ethanol distilled from sugarcane, and lignocellulose filler from waste generated in the processing of sponge gourds for bathing use. The composites were prepared with 10, 20, 30, and 40%wt of filler in a twin-screw extruder. The materials were analyzed in a parallel plate rheometer and a melt-flow indexer. The composite morphology was determined by scanning electron microscopy. The composite viscosity increased with filler content, suggesting possible formation of filler agglomerates. This result was confirmed by Cole-Cole diagrams.

Introduction: Acrylonitrile-butadiene-styrene copolymer (ABS) and high impact polystyrene (HIPS) are plastics typically found in waste electrical and electronic equipment (WEEE or e-waste). As such, recycling is a beneficial method for reintroducing polymeric materials from electrical and electronic equipment to the same production cycle. This study aimed to investigate mechanical recycling of ABS and HIPS from WEEE reprocessed six times, totaling 24 cycles.Methods: Reprocessing was performed by extrusion and test specimens were obtained by injection. The technical aspects assessed before and after reprocessing were mechanical properties (tensile, flexural and impact strength), thermogravimetric analysis (TGA), Fourier-transform infrared spectroscopy (FTIR) and melt flow index (MFI), compared with those of reprocessed virgin polymeric materials. The environmental aspect was evaluated by monitoring energy consumption and solid waste generation during each reprocessing cycle.Results: Average energy consumption per extrusion and injection cycle was 0.7 and 2.0 kW/kg, respectively. There was a 30% increase in MFI from the first to sixth reprocessing cycle for virgin HIPS (5.5 g/10 min in 200°C and 5 kg), the largest among the polymers. The values for virgin ABS (6.0 g/10 min in 200°C and 5 kg) and ABS and HIPS from WEE increased by 11–15% from the first to sixth cycle. Impact strength was affected from the second reprocessing cycle onwards for ABS e-waste (14% decrease) and in the fifth cycle (16% decrease) for HIPS e-waste.Discussion: The thermal, tensile and flexural properties of the virgin and post-consumer materials remained almost unchanged as the number of reprocessing cycles increased, indicating that these materials have the potential and properties for reintroduction into the same production cycle.