Background and Objectives: The aim of this study is to evaluate the efficacy of an autologous dentin graft, via extracted teeth that are processed into bacteria-free particulate dentin in a Smart dentin grinder and then grafted immediately into alveolus post extraction or into bone deficiencies. Materials and Methods: Ten healthy, partially edentulous patients with some teeth in the mandible were recruited in the study. After their own teeth were grinded, particulate teeth were placed in empty sockets and bone defects after teeth extractions. Furthermore, after three, six, 12 and 24 months, core samples using a 3 mm trephine were obtained. Results: At three months, the particles of grinded tooth were immersed inside a new connective tissue with a small new bone formation (16.3 ± 1.98). At six months, we observed small particles of dentin integrated in new immature bone, without inflammation in the soft tissue (41.1 ± 0.76). At twelve months, we observed a high amount of bone formation surrounding tooth particles (54.5 ± 0.24), and at twenty-four months, new bone, a big structure of bone, was observed with dentin particles (59.4 ± 1.23), statistically different when compared it with at three months. Conclusions: A particulate dentin graft should be considered as an alternative material for sockets’ preservation, split technique, and also for sinus lifting. One of the special characteristics after 24 months of evaluation was the high resorption rate and bone replacement without inflammation. This material could be considered as an acceptable biomaterial for different bone defects due to its osteoinductive and osteoconductive properties

Closure of the surgical incision has been the primary function of sutures since their introduction. However, whatever the type, they are known to carry bacteria, which can be a source of infection. Five types of surgical sutures, Gut, Silk, Vicryl, PTFE, and Polyamide, were selected and tested on their ability to carry aerobic and anaerobic bacteria and were rated on the basis of forming colony-forming units (CFUs). Aerobic bacteria grown around gut sutures showed minimum CFUs (≈30 × 10⁴/suture). Though very less anaerobic bacteria growth was seen among all tested suture materials, it was maximum around Vicryl and polyamide sutures. Every suture material is capable, albeit not equally, of holding bacterial biofilm formation, which can be a source of surgical site infection.

The aim of the study was to evaluate the chemical composition of crushed, extracted human teeth and the quantity of biomaterial that can be obtained from this process. A total of 100 human teeth, extracted due to trauma, decay, or periodontal disease, were analyzed. After extraction, all the teeth were classified, measured, and weighed on a microscale. The human teeth were crushed immediately using the Smart Dentin Grinder machine (KometaBio Inc., Cresskill, NJ, USA), a device specially designed for this procedure. The human tooth particles obtained were of 300–1200 microns, obtained by sieving through a special sorting filter, which divided the material into two compartments. The crushed teeth were weighed on a microscale, and scanning electron microscopy (SEM) evaluation was performed. After processing, 0.25 gr of human teeth produced 1.0 cc of biomaterial. Significant differences in tooth weight were found between the first and second upper molars compared with the lower molars. The chemical composition of the particulate was clearly similar to natural bone. Scanning electron microscopy–energy dispersive X-ray (SEM–EDX) analysis of the tooth particles obtained mean results of Ca% 23.42 ± 0.34 and P% 9.51 ± 0.11. Pore size distribution curves expressed the interparticle pore range as one small peak at 0.0053 µm. This result is in accordance with helium gas pycnometer findings; the augmented porosity corresponded to interparticle spaces and only 2.533% corresponded to intraparticle porosity. Autogenous tooth particulate biomaterial made from human extracted teeth may be considered a potential material for bone regeneration due to its chemical composition and the quantity obtained. After grinding the teeth, the resulting material increases in quantity by up to three times its original volume, such that two extracted mandibular lateral incisors teeth will provide a sufficient amount of material to fill four empty mandibular alveoli. The tooth particles present intra and extra pores up to 44.48% after pycnometer evaluation in order to increase the blood supply and support slow resorption of the grafted material, which supports healing and replacement resorption to achieve lamellar bone. After SEM–EDX evaluation, it appears that calcium and phosphates are still present within the collagen components even after the particle cleaning procedures that are conducted before use.

Soon after tooth extraction the bone resorption takes place reducing the height and width of alveolar ridge. This produces an altered morphology of the bone unfavorable for implant placement and implant placement becomes impossible without surgical correction. Socket grafting maintains and preserves ridge for implant placement. How to cite this article Mahesh L, Narayan TV, Bali P, Shukla S. Socket Preservation with Alloplast: Discussion and a Descriptive Case. J Contemp Dent Pract 2012;13(6):934-937.

Extraoral cementation is a technique that utilizes a stock abutment and a laboratory fabricated crown that is cemented extra orally; the advantage of this technique is that the retained excess luting agent during intraoral cementation, which can be a source of bacterial retention and cannot be observed radio graphically and is not possible to remove with explorer all the time, does not get accumulated and can be trimmed off easily before the final placement of the crown. Thus this technique allows no retention of luting cement, providing better soft tissue contours, no soft tissue inflammation, no retention of plaque and no bone loss. In short it prevents implant failure related to retained cement around implants. This technique provides overall health of peri-implant soft tissues as compared to conventional technique of crown placement where cement retention is a common problem, leading to implant failures.