Poly(L-lactide) (PLLA)/polyethylene glycol (PEG) mixed solutions were successfully electrospun into micro-or nanofibrous polymer mats. The fiber diameter was in the range 100nm-6μm. The effect of the concentration of the spinning solutions and the ratio of PLLA/PEG on the fiber diameter and morphology was investigated. The hydrophilicity was tuned by varying the PLLA/PEG ratio. The tissue compatibility of the electrospun nanofibrous scaffolds was screened using two different cell models of human dermal fibroblasts and the osteoblast-like cell line MG-63. Both types of cells attached uniformly and approximately equally to all PLLA/PEG nanofibers. In long-term cultures osteoblast-like cells tend to spatially organize in tissue-like structure, particularly within the scaffold with the highest PEG content (PLLA/PEG at weight ratio 70/30). These results indicate that PLLA mixed with hydrophilic PEG produces a promising new biocompatible material for engineering scaffolds.

The effect of the electrospinning process parameters on the morphology, alignment, and self-organization of the fibers into bundles and/or yarns are outlined. The fabrication of polylactide materials containing ionic drugs by electrospinning is emphasized. The main approaches used for the preparation of electrospun drug-loaded materials: electrospinning of a mixed solution containing the polymer(s) and the drug(s) or dual spinneret electrospinning of separate drug-containing solutions are compared. The latter approach allows the obtaining of drug-loaded fibrous materials while avoiding the drug interaction. The potential application of the obtained materials containing ionic drugs as wound dressings is outlined.

Electrospinning is a promising method for producing polymer materials composed of micro- and nanosized fibers. This method allows the preparation of random and aligned fibers of different morphologies, such as cylindrical or ribbon-shapes, defect-free or with defects, and with or without pores or porous. The increasing number of studies on electrospinning requires a set of criteria for more complex evaluation of the fiber morphology and the topology of these polymer materials to be established. The main characteristics necessary for a complex evaluation of the morphology of electrospun micro- and nanofibers have been systematized in this paper. Examples of characterization of the morphology and of the alignment of various micro- and nanofibers are given.