MOF–derived porous carbon is a type of promising catalyst to replace expensive Pt–based catalysts for oxygen reduction reaction (ORR). The catalytic activity for ORR depends closely on pyrolysis conditions. In this work, a Co–doped ZIF–8 material was chosen as a research object. The effect of pyrolysis conditions (temperature, heating rate, two–step heating) on the ORR performance of ZIF–derived carbon catalysts was systematically studied. The Co–ZIF–8 catalyst carbonized at 900 °C exhibits better ORR catalytic activity than that carbonized at 800 °C and 1000 °C. Moreover, a low heating rate can enhance catalytic activity. Two–step pyrolysis is proven to be an effective way to improve the performance of catalysts. Reducing the heating rate in the low–temperature stage is more beneficial to the ORR performance, compared to the heating rate in the high–temperature stage. The results show that the Co–ZIF–8 catalyst exhibits the best performance when the precursor was heated to 350 °C at 2 °C/min, and then heated to 900 °C at 5 °C/min. The optimum Co–ZIF–8 catalyst shows a half–wave potential of 0.82 V and a current density of 5.2 mA·cm⁻² in 0.1 M KOH solution. It also exhibits high content of defects and good graphitization. TEM mapping shows that Co and N atoms are highly dispersed in the polyhedral carbon skeleton. However, two–step pyrolysis has no significant effect on the stability of the catalyst.

Titanium alloys are widely used in marine engineering and other industries. To broaden their application, a novel (α + β) titanium alloy Ti−6Al−3Mo−2Zr−2Fe was studied in this work. A tube with an outer diameter of 60mm, inner diameter of 38 mm, and length of 500 mm was produced by ingot metallurgy and hot extrusion. The microstructure, mechanical properties, and corrosion resistance of the tube were systematically analyzed. The as−extruded Ti−6Al−3Mo−2Zr−2Fe alloy exhibited a typical duplex microstructure. EBSD observation showed that a strong <$10 \overline{1}0$>//RD fiber texture of an α phase with a close−packed hexagonal structure was formed in the radial direction. The transformation temperature T_β was determined to be 880–890 °C. A duplex microstructure with fine α platelets was obtained when the alloy was solution−treated at 850 °C for 1 h and underwent an aging treatment at 550 °C for 6 h. The room−temperature tensile strength and elongation of the aged alloy reached 1081.5 MPa and 6.5%, respectively. The corrosion resistance was tested by open circuit potential and a potentiodynamic polarization curve. The results show that the corrosion resistance of the Ti−6Al−3Mo−2Zr−2Fe alloy was better than that of the commonly used TC4 alloy in both a 3.5% NaCl solution and an acidic solution.