Superhydrophobic coatings are beneficial for applications like self-cleaning, anti-corrosion, and drag reduction. In this study, we investigated the impact of surface geometry on the static, dynamic, and sliding contact angles in the Cassie–Baxter state. We used fluoro-silane-treated silicon micro-post patterns fabricated via lithography as model surfaces. By varying the solid fraction (ϕ_s), edge-to-edge spacing (L), and the shape and arrangement of the micro-posts, we examined how these geometric factors influence wetting behavior. Our results show that the solid fraction is the key factor affecting both dynamic and sliding angles, while changes in shape and arrangement had minimal impact. The Cassie–Baxter model accurately predicted receding angles but struggled to predict advancing angles. These insights can guide the development of coatings with enhanced superhydrophobic properties, tailored to achieve higher contact angles and customized for different environmental conditions.

The effect of particle loading on the wetting properties of coatings was investigated by modifying a coating formulation based on hydrophilic silica nanoparticles and poly (acrylic acid) (PAA). Water contact angle (WCA) measurements were conducted for all coatings to characterize the surface wetting properties. Wettability was improved with an increase in particle loading. The resulting coatings showed superhydrophilic (SH) behavior when the particle loading was above 53 vol. %. No new peaks were detected by attenuated total reflection (ATR-FTIR). The surface topography of the coatings was studied by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The presence of hydrophilic functional groups and nano-scale roughness were found to be responsible for superhydrophilic behavior. The surface chemistry was found to be a primary factor determining the wetting properties of the coatings. Adhesion of the coatings to the substrate was tested by tape test and found to be durable. The antifogging properties of the coatings were evaluated by exposing the films under different environmental conditions. The SH coatings showed anti-fogging behavior. The transparency of the coatings was significantly improved with the increase in particle loading. The coatings showed good transparency (>85% transmission) when the particle loading was above 84 vol. %.

With production of nanocomposites, the product life cycle, including recycling, becomes critical.

Superhydrophilic coatings based on a hydrophilic silica nanoparticle suspension and Poly (acrylic acid) (PAA) were prepared by dip coating. Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM) were used to examine the morphology of the coating. The effect of surface morphology on the dynamic wetting behavior of the superhydrophilic coatings was studied by changing the silica suspension concentration from 0.5% wt. to 3.2% wt. while keeping the silica concentration in the dry coating constant. The droplet base diameter and dynamic contact angle with respect to time were measured using a high-speed camera. A power law was found to describe the relationship between the droplet diameter and time. A significantly low experimental power law index was obtained for all the coatings. Both roughness and volume loss during spreading were suggested to be responsible for the low index values. The water adsorption of the coatings was found to be the reason for the volume loss during spreading. The coatings exhibited good adherence to the substrates and retention of hydrophilic properties under mild abrasion.