We present small-angle neutron scattering data proving that, on the insulating side of the metal-insulator transition, the doped perovskite cobaltite ${\mathrm{L}\mathrm{a}}_{1-x}{\mathrm{S}\mathrm{r}}_x{\mathrm{C}\mathrm{o}\mathrm{O}}_3$ phase separates into ferromagnetic metallic clusters embedded in a nonferromagnetic matrix. This induces a hysteretic magnetoresistance, with temperature and field dependence characteristic of intergranular giant magnetoresistance (GMR). We argue that this system is a natural analog to the artificial structures fabricated by depositing nanoscale ferromagnetic particles in a metallic or insulating matrix; i.e., this material displays a GMR effect without the deliberate introduction of chemical interfaces.

In the present study, we investigate the mucoadhesive characteristics and release of the anticancer agent curcumin, contained in chitosan nanoparticles (CS-NPs). Such a system has potential therapeutic benefits in the treatment of colon cancer through prolonged retention and delivery. The CS-NPs were ionically gelled with tripolyphosphate (TPP) and registered an isoelectric pH of 6.2 (z-average diameter of 214 nm ± 1.0 nm). pH variations around the isoelectric point caused a reduction in CS-NPs electrical charge which correspondingly increased the z-average due to agglomeration. Curcumin release from CS-NPs was slowest at chitosan to TPP weight ratio of 3:1, with a significant retention (36%) at the end of 6 h. Adsorption isotherms of mucin on CS-NPs fitted both the Freundlich and Langmuir models, suggesting a monolayer-limited adsorption on heterogeneous sites with varied affinities. Encapsulated curcumin exerted an influence on the adsorption of mucin due to H-bonding as well as π-π interactions between the phenolic moieties of curcumin and mucin.