Nanotechnology is playing a pivotal role in improving quality of life due to its versatile applications in many areas of research. In this regard, nanoparticles have gained significant importance. Zinc oxide nanoparticles (ZnO NPs) amongst other nanoparticles are being used in producing nanocomposites. Methods like solvent casting, solution casting, solvent volatilization, twin-screw extrusion, melt compounding and extrusion blow molding have been applied to produce ZnO NPs based (bio)polymer composites. These composites are of great interest in the research area of food packaging materials due to their improved multifunctional characteristics like their mechanical, barrier and antimicrobial properties. This paper gives an overview of the main methods to synthesize ZnO NPs, methods to incorporate ZnO NPs in (bio)polymers, and finally, the gas barrier and mechanical properties of the nanocomposites. As a conclusion, a maximum decline in oxygen, carbon dioxide and water vapor permeability was reported as 66%, 17% and 38% respectively, while tensile strength and young’s modulus were observed to increase by 32% and 57% respectively, for different (bio)polymer/ZnO nanocomposites.

Ultrasonic spray-coating (USSC)—a wet chemical deposition method to deposit ultrathin (down to 20 nm) coatings—is being applied as a promising alternative deposition method for functional coatings due to an economical, simple, and precise coating process with easy control over its operating parameters. In this research, zinc oxide nanoparticles (ZnO NPs) were ultrasonically spray-coated on commercial-grade polyethylene terephthalate (PET) and poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) films. The most suitable parameters for the ink composition, the ultrasonic spray-coating process, and the number of coating passes (up to 50×) were selected on the basis of a series of experiments. The oxygen gas barrier properties in terms of the oxygen transmission rate (OTR) of neat PET, and 3×, 5×, 10×, and 50× ZnO NP-coated PET and PHBHHx substrates were investigated. The OTR values for neat PET, and 3×, 5×, and 10× ZnO NP-coated PET substrates were found to be the same; however, a 5% reduction in OTR for 50× ZnO NP-coated PET substrate was observed compared to the neat PET substrate. No reduction in OTR was found for any above number of coating passes on PHBHHx substrates against the neat PHBHHx substrate. However, the ultraviolet (UV) tests of 3×, 5×, and 10× ZnO NP-coated PET and PHBHH× substrates revealed a significant decrease in percentage transmission for 10× coated PET and PHBHHx substrates as compared to their 3× and 5× ZnO NP-coated substrates, respectively. It was revealed from the study that the 50× ZnO NP coating of the PET substrate created a slight difference in OTR as compared to the reference substrate. However, the ultrasonic spray-coating method created a significant UV barrier effect for 3×, 5×, and 10× ZnO NP-coated PET and PHBHHx substrates, which demonstrates that the optimized coating method cannot be used to create a high oxygen barrier but can certainly be applied for UV barrier applications in food packaging. It is concluded that ultrasonic spray deposition of ZnO NPs on PET and PHBHHx materials has shown promising results for UV barrier properties, demonstrating the advantages of using this method compared to other coating methods with regard to cost-effectiveness, precise coating, and better process control.