We present the results of one year observation of wetting and corrosion properties of nanosecond fiber laser-textured stainless steel, uncoated and coated with epoxy or FAS (fluoroalkylsilane)-TiO₂/epoxy. A comparative study was performed on samples kept under ambient conditions and in reduced air pressure and humidity. The results show the ability to induce wettability conversion from initially superhydrophilic to final superhydrophobic state either indirectly by ageing the uncoated laser-textured surface or directly by application of FAS-TiO₂/epoxy coating. The storage conditions significantly influenced the wettability development of uncoated laser-textured steel, i.e., the process of ageing was slowed down in reduced air pressure and humidity. Detailed surface chemical analysis revealed that adsorption of the organic matters from the surrounding media influences the wettability conversion and ageing. However, the ageing of the coated surfaces was not affected by the storage conditions. Corrosion stability of uncoated laser-textured surfaces was enhanced over time due to the wettability transition, depending on their morphology. Coatings represent a superior barrier over the texture and wettability with the stable long-term surface protection against aggressive media.

The elucidation of spontaneous growth of metal whiskers from metal surfaces is still ongoing, with the mainstream research conducted on Sn whiskers. This work reports on the discovery of Pb whisker growth from Bi-Mg-Pb solid pools found in common machinable aluminum alloy. The whiskers and hillocks display unique morphologies and complex growth that have not been documented beforehand. In contrast to typical understanding of whisker growth, the presented Pb whiskers show a clear nanocrystalline induced growth mechanism, which is a novel concept. Furthermore, the investigated whiskers are also found to be completely composed of nanocrystals throughout their entire length. The performed research gives new insight into nucleation and growth of metal whiskers, which raises new theoretical questions and challenges current theories of spontaneous metal whisker growth. Additionally, this work provides the first microscopic confirmation of recrystallization growth theory of whiskers that relates to oriented attachment of nanocrystals formed within an amorphous metallic matrix. The impact of mechanical stress, generated through Bi oxidation within the pools, is theoretically discussed with relation to the observed whisker and hillock growth. The newly discovered nanocrystalline growth provides a new step towards understanding spontaneous metal whisker growth and possibility of developing nanostructures for potential usage in sensing and electronics applications.