To decrease the environmental impact of the construction industry, energy-efficient insulation materials with low embodied production energy are needed. Lime-hemp concrete is traditionally recognized as such a material; however, the drawbacks of this type of material are associated with low strength gain, high initial moisture content, and limited application. Therefore, this review article discusses alternatives to lime-hemp concrete that would achieve similar thermal properties with an equivalent or lower environmental impact. Binders such as gypsum, geopolymers, and starch are proposed as alternatives, due to their performance and low environmental impact, and available research is summarized and discussed in this paper. The summarized results show that low-density thermal insulation bio-composites with a density of 200–400 kg/m³ and thermal conductivity (λ) of 0.06–0.09 W/(m × K) can be obtained with gypsum and geopolymer binders. However, by using a starch binder it is possible to produce ecological building materials with a density of approximately 100 kg/m³ and thermal conductivity (λ) as low as 0.04 W/(m × K). In addition, a preliminary life cycle assessment was carried out to evaluate the environmental impact of reviewed bio-composites. The results indicate that such bio-composites have a low environmental impact, similar to lime-hemp concrete.

This study aimed to determine the impact of the initial temperature of the paste (from 5 °C to 35 °C) and the addition of water, which reflects a decrease in the molarity of activation solutions (AS) by diluting 10 M NaOH with distillate water, on the rheological properties of geopolymer pastes. Additionally, this resulted in changes to the physical–mechanical properties of geopolymers after curing. A higher amount of water in the AS composition and higher initial paste temperature led to an increase in the spread values up to 28% and decreases viscosity. A smaller amount of water in the AS composition and a higher initial paste temperature accelerated the speed of the geopolymer structure formation up to 1.5 times during the curing period, increased compressive strength and reduced apparent porosity and pore size. X-ray diffraction confirmed the compressive strength test results and revealed that the lower amount of water in the AS and the higher initial paste temperature for the geopolymer preparation significantly affected the mineral formation and physical and mechanical properties of the samples.

According to European regulations, the construction industry supports and strives to save non-renewable natural resources, increases the share of reusable resources in production and attempts to use renewable natural resources as much as possible by creating alternative building materials, such...