This study successfully synthesized fluorinated silicon-containing waterborne polyurethanes (FSWPUs) by using polycaprolactone (PCL) diol, 2,2,3,3-Tetrafluoro-1,4-butanediol, and [3-(2-Aminoethylamino)propyl] trimethoxysilane (AEAPTES ). The FSWPU’s particle size was examined using dynamic light scattering. After the FSWPUs were processed into a dry film, their molecular weight and basic properties were analyzed using gel permeation chromatography (GPC), Fourier-transform infrared spectroscopy (FTIR), and energy-dispersive X-ray spectroscopy (EDS). Additionally, the thermal stability of the FSWPUs was inspected by thermogravimetric analysis and dynamic mechanical analysis. The tensile strength and elongation at the break of the FSWPUs before and after hydrolysis were also analyzed, using a tensile testing machine. Subsequently, FSWPU emulsions were cast between the tiles, and hydrophilicity, hydrophobicity, and surface tension were then measured on a contact-angle measurement instrument. The tensile testing machine was again employed to test the sheer strength of the FSWPUs between the tiles, and a tape test was conducted to analyze their adhesion to the tiles. The results revealed that AEAPTES functional groups can reinforce the thermal stability, tensile strength, and water resistance of FSWPUs. Moreover, the AEAPTES functional groups increased the adhesion of FSWPUs to the tiles and reduced the surface energy of the tiles.

According to Taiwan’s Ministry of the Interior, from 2017 to 2019, more than 12% of house-purchase disputes were due to water leakage caused by frequent tropical rains, which have long troubled engineers. The thermal stability resistance, water resistance, and ultraviolet resistance of existing polyurethane formulations have been limited by environmental aging. Thus, the lifespan of commercial PU-coated resins (typical PU) for the waterproofing of roof surfaces is merely two to three years. Accordingly, this study proposed the introduction of siloxane and imide groups to produce waterborne poly(urethane-siloxane-imide) (Si-imide-WPU) copolymers to improve the resistance of environmental aging in typical PU. The waterproof coating resin made of Si-imide-WPU copolymers was environmentally friendly, safe to use, and free of organic solvents. The results showed that the optimal Si-imide-WPU-2 sample in the study made improvements on the defects of polyurethane (PU) including its thermal properties, mechanical properties, environmental resistance, and lifespan which could be extended up to 5.4 years. Consequently, the studied Si-imide-WPU copolymers could reduce material waste while enhancing the sustainability and efficiency of the architecture.

Due to rapid technological advancements, firms are paying more attention to the importance of knowledge creation and sharing. Effective knowledge management can be utilized to enhance employee performance, as well as an organization’s competitiveness. Staff training is crucial to the internal knowledge transfer within an organization. Through education and training, an organization can transfer its internal knowledge to its employees. Furthermore, the use of information systems to assist in training and management has been widely adopted by organizations. This study, through action research, attempted to understand how organizations can build a Wiki system to assist in the training of new staff. When employees can obtain work knowledge from more sources, it is easier for the knowledge to be shared and transferred during training. The results show that in the process of implementing Wiki system, providing support for Wiki software design, management skill, and a knowledge sharing environment can enable employees to create and exchange knowledge. The organization itself can rapidly accumulate knowledge capital and enhance the quality of staff through such system in order to enhance its competitiveness.