The Lotsberg Salt Formation (LSF) of the Lower Devonian age occupies a large area in Alberta (Canada). It has been used for brine production, disposal, and storage purposes since the 1950s. Its petrological and geochemical features remain poorly understood up to now. Previous studies showed that these salt rocks are large crystalline and distinguishable by a very low bromine content (2–5 ppm). Our studies reveal that the main impurity is dolomite with an addition of haematite. It showed, also, a lack of sulphate minerals (anhydrite). Manganite also occurs within the halite crystals. Microthermometric measurements of primary fluid inclusions in halite show a large range of homogenization temperatures from 32.4 °C to 357.0 °C with the highest temperature in the upper part of the salt profile. Geochemical analysis confirms the low bromine contents, which is between 0.67–12.74 ppm. Potassium contents (166–3651 ppm) seem to be in the normal range for salt rocks, but magnesium content (25–177 ppm) is much lower than potassium. Rubidium is, as well, within the normal range, with values between <0.01 ppm and 3.13 ppm, while caesium contents (5.07–211.22 ppm) are almost sixty times higher in comparison to those of rubidium. The high concentration of Cs, Mn, Rb, and the high homogenization temperatures of the host minerals suggest that the LSF underwent extensive ion exchange related to hydrothermal inflow. These hydrothermal solutions originated from the basement of the LSF.

Agate samples collected from the vicinity of Asni and Agouim (Western Atlas, Morocco) were investigated using microscopic observations supported by Raman micro-spectroscopy. The agates are marked by the presence of various microtextures typical of epithermal vein deposits, including jigsaw-puzzle, feathery, and lattice-bladed. The first two indicate that the formation of agates was likely marked by recrystallization of metastable silica phases (i.e., opaline silica or massive chalcedony). The presence of lattice-bladed (after barite and calcite) quartz may be, in turn, ascribed to the boiling-related conditions that could have triggered the formation of abundant copper and iron sulfides found within silica matrix. Additionally, the local occurrence of growth lines (so-called Bambauer quartz) and intergrowth of length-slow and length-fast chalcedony are linked to the variations of physico-chemical conditions during rock formation (alkaline-acidic). According to Raman spectroscopy, silica matrix of the agates is made of α-quartz with a local admixture of moganite (from 0.0 up to 78 wt.%), but also contains numerous solid inclusions of hematite, celadonite, as well as poorly-organized carbonaceous material and rutile. These phases were likely emplaced during low-temperature hydrothermal activity of SiO₂-bearing fluids that originated from post-magmatic hydrothermal activity developed within host rocks and/or meteoric waters.

Outcrops of natural blue and purple halite crystals have been found in Kłodawa (Poland) salt deposit originating from the Permian (Zechstein) salt formation within tectonic zones. Field works carried out on various levels of Kłodawa Salt Mine indicated differences both in intensity of the hue and in the size of the outcrops. Their occurrence was connected with the presence of epigenetic sediments rich in potassium. For the samples of blue halite, an optical anisotropy (birefringence) was observed for both standard mineralogical thin sections and thick plates, indicating a deviation from cubic symmetry. The blue colouration of the halites, described by ultraviolet–visible spectroscopy, is due to the presence of colour centres. The colour centres have been recently identified as: F, R₁ (F₃), R₂ (F₃), M and plasmons (Wesełucha-Birczyńska et al., Vib Spectrosc 60:124–128, 2012). The trace amount of impurities detected in the blue halites by means of scanning electron microscopy–energy dispersive X-ray spectroscopy and micro-X-ray fluorescence techniques were connected mainly with solid inclusions such as K _x Na_{(1 − x)}Cl, KMgCl₃·6H₂O, KCl, orthorhombic sulphur, quartz and some other phases like pyrite. Crystallographic data obtained by X-ray diffraction experiments for the single crystals of the halite from Kłodawa with different saturation of blue or purple colours, as well as for natural colourless halite, revealed lowering of space-group symmetry to monoclinic, orthorhombic, trigonal, tetragonal or even triclinic systems while the space group typical for pure NaCl is Fm-3m.