This article presents the results of experimental research on the effect of high-speed machining (HSM) in the milling process on the tool wear, surface layer properties, and fatigue life of objects made of Ti-6Al-4V titanium alloy. Titanium alloys are widely used in many industries due to their high strength-to-density ratio, corrosion resistance, and resistance to dynamic loads. The experiment was conducted on a vertical three-axis machining centre, Avia VMC800HS. The influence of increased cutting speeds on the average values and amplitudes of the total cutting force components and the surface roughness of the machined workpiece was determined. Variable cutting speeds v_c = 70; 130; 190; 250; 310 m/min were applied. The impact of HSM on machinability indicators, such as the microhardness of the surface layer, the distribution of residual stresses, and the fatigue life of the samples after milling, was analysed. The thickness of the hardened layer varied from 20 to 28 micrometres. The maximum compressive residual stress Ϭ_m = 190 MPa was achieved at the speed of v_c = 190 m/min. A significant influence of increased cutting speeds on tool wear was demonstrated. The longest tool life (t = 70 min) was obtained for low cutting speeds (conventional) v_c = 70 m/min.

This paper presents results of ultrasonic non-destructive testing of carbon fibre-reinforced plastics (CFRPs) and glass-fibre reinforced plastics (GFRPs). First, ultrasonic C-scan analysis was used to detect real defects inside the composite materials. Next, the composite materials were subjected to drilling in the area of defect formation, and measured forces were used to analyse the drilling process using recurrence methods. Results have confirmed that recurrence methods can be used to detect defects formed inside a composite material during machining.

This paper presents the results of an experimental study on the impact of slide burnishing on surface roughness parameters (Sa, Sz, Sp, Sv, Ssk, and Sku), topography, surface layer microhardness, residual stress, and mean positron lifetime (τ_mean). In the study, specimens of X6CrNiTi18 stainless steel were subjected to slide burnishing. The experimental variables were feed and slide burnishing force. The slide burnishing process led to changes in the surface structure and residual stress distribution and increased the surface layer microhardness. After slide burnishing, the analyzed roughness parameters decreased compared with their pre-treatment (grinding) values. The slide burnishing of X6CrNiTi18 steel specimens increased their degree of strengthening e from 8.77% to 42.74%, while the hardened layer thickness g_h increased after the treatment from about 10 µm to 100 µm. The maximum compressive residual stress was about 450 MPa, and the maximum depth of compressive residual stresses was g_σ = 1.1 mm. The positron mean lifetime τ_mean slightly yet systematically increased with the increase in burnishing force F, while an increase in feed led to changes of a different nature.

This paper set out to investigate the effect of cutting speed v_c and trochoidal step s_tr modification on selected machinability parameters (the cutting force components and vibration). In addition, for a more detailed analysis, selected surface roughness parameters were investigated. The research was carried out for two grades of magnesium alloys—AZ91D and AZ31—and aimed to determine stable machining parameters and to investigate the dynamics of the milling process, i.e., the resulting change in the cutting force components and in vibration. The tests were performed for the specified range of cutting parameters: v_c = 400–1200 m/min and s_tr = 5–30%. The results demonstrate a significant effect of cutting data modification on the parameter under scrutiny—the increase in v_c resulted in the reduction of the cutting force components and the displacement and level of vibration recorded in tests. Selected cutting parameters were modelled by means of Statistica Artificial Neural Networks (Radial Basis Function and Multilayered Perceptron), which, furthermore, confirmed the suitability of neural networks as a tool for prediction of the cutting force and vibration in milling of magnesium alloys.

This paper attempts to compare regular shot peening (RSP) and semi-random shot peening (SRSP). A characteristic of the first method is that the peening elements hit the treated surface in sequence, with a regular distance maintained between the dimples. The other method (SRSP) is a controlled modification of the shot-peening process, which is random by nature. The shot-peening method used in this study differs from conventional shot peening (shot blasting and vibratory shot peening) in that it allows controlled and repeatable determination of the configuration and distribution of impacts exerted by the peening element on the workpiece surface, which makes the process more repeatable and easier to model. Specimens of EN-AW 7075 aluminum alloy were used for testing. The following variables were used in the experiments: ball diameter, impact energy, and distance between the dimples. Microhardness distribution in the surface layer, 2D surface roughness, and surface topography were analyzed. FEM simulations of the residual stress distribution in the surface layer were performed. It has been found that regular shot peening results in reduced surface roughness, while semi-random shot peening leads to higher surface layer hardening.

Measurements of forces during machining, especially thin-walled structures typical of the aviation industry, are important in the aspect of instability caused by vibration. One of the last stages of manufacturing by machining is the finishing treatment and deburring of the product’s edges. Brushes with ceramic fibres are often employed in deburring, especially for large-sized elements specific to the aviation industry due to the possibility of automatic machining directly on machining centres. This study set out to analyse the effect of variable brushing conditions on axial forces and the selected surface layer properties of AW-7075 aluminium alloy. Experimental studies have examined factors such as surface roughness and topography, axial cutting force in ceramic brush treatment and surface free energy in the aspect of adhesive joints. The tested variable process parameters were the fibre material and the adjustment sleeve spring stiffness. Based on the tests, it was found that the axial force applied by the brush was more strongly connected with the spring stiffness rather than the type of bristle. For most cases, an increase in the value of free surface energy after brushing was observed compared to the initial machining which was milling.