In the present work, we synthesized Co_xZn_1-xFe₂O₄ spinel ferrite nanoparticles (x= 0, 0.1, 0.2, 0.3 and 0.4) via the precipitation and hydrothermal-joint method. Structural parameters were cross-verified using X-ray powder diffraction (XRPD) and electron microscopy-based techniques. The magnetic parameters were determined by means of vibrating sample magnetometry. The as-synthesized Co_xZn_1-xFe₂O₄ nanoparticles exhibit high phase purity with a single-phase cubic spinel-type structure of Zn-ferrite. The microstructural parameters of the samples were estimated by XRD line profile analysis using the Williamson–Hall approach. The calculated grain sizes from XRPD analysis for the synthesized samples ranged from 8.3 to 11.4 nm. The electron microscopy analysis revealed that the constituents of all powder samples are spherical nanoparticles with proportions highly dependent on the Co doping ratio. The Co_xZn_1-xFe₂O₄ spinel ferrite system exhibits paramagnetic, superparamagnetic and weak ferromagnetic behavior at room temperature depending on the Co²⁺ doping ratio, while ferromagnetic ordering with a clear hysteresis loop is observed at low temperatures (5K). We concluded that replacing Zn²⁺ ions with Co²⁺ ions changes both the structural and magnetic properties of ZnFe₂O₄ nanoparticles.

Ultrasonically cleaned glass slides are used as substrates for receiving the different thickness of Zinc selenide (ZnSe) films. The deposition processes of our investigated films were done at room temperature using physical thermal evaporation mechanism under vacuum ≈2 × 10⁵ mbar. We investigated the optical and structural parameters of ZnSe thin films in correlation with film thickness (200–650 nm). Various techniques such as UV–vis-NIR spectrophotometer, x-ray diffraction lines and field emission scanning electron microscope were used to investigate aforementioned parameters. Structural analysis indicate that the films exhibited cubic preferred orientation along the plane (111) and the crystallinity and crystallite size of films increases linearly with film thickness. The optical band gap ranges from 2.69 to 2.81 eV and it is founded that it increases with film thickness. According to the applied Swanepoel’s approach, it is possible to estimate the optical parameters and average thickness of the ZnSe thin films of different thicknesses with higher accuracy.