Mo-modified ZSM-5 catalysts were prepared and used to produce aromatic hydrocarbons during catalytic fast pyrolysis (CFP) of biomass. The composition and distribution of aromatics were investigated on pyrolysis–gas chromatography/mass spectrometry (Py-GC/MS). The reaction factors, such as the Mo content, the reaction temperature and the catalyst/biomass mass ratio, were also optimized. It was found that the 10Mo/ZSM-5 catalyst displayed the best activity in improving the production of monocyclic aromatic hydrocarbons (MAHs) and decreasing the yield of polycyclic aromatic hydrocarbons (PAHs) at 600 °C and with a catalyst/biomass ratio of 10. Furthermore, according to catalyst characterization and the experiment results, the aromatics formation mechanism over Mo/ZSM-5 catalysts was also summarized and proposed.

The doping of PP (polypropylene) with cotton straw improved the bio-oil yield, which showed there was a synergy in the co-pyrolysis of the cotton straw and PP at the range of 380–480 °C. In a fixed-bed reactor, model compounds and co-pyrolysis products were used for reactants of hydrodeoxygenation (HDO) over Ni-Mo/Al2O3. The deoxygenation rate of model compounds decreased over Ni-Mo/Al2O3 in the following order: alcohol > aldehyde > acetic acid > ethyl acetate. The upgraded oil mainly consisted of C11 alkane.

An environmentally friendly catalyst and task-specific ionic liquid (IL), 1-(4-sulfonic acid) butyl-3-cetyl-2-methyl imidazolium hydrogen sulfate, was applied to the dehydration of xylose to furfural. Its structure was determined by FT-IR, ¹H NMR technologies. The solubility of IL in water changed with the temperature, and had the advantages of homogeneous and heterogeneous catalysts. At the given conditions, xylose conversion of 95.3% and furfural yield of 67.5% were achieved over IL.

A series of gallium-containing MFI (Ga-MFI) zeolites with varying Ga₂O₃/Al₂O₃ ratios were synthesized using hydrothermal synthesis and tested as catalyst in catalytic fast pyrolysis (CFP) of beech wood for aromatic production. The results show that the incorporation of Ga slightly reduced the effective pore size of Ga-MFI zeolites compared to conventional HZSM-5 zeolites. Therefore, the Ga-MFI zeolites increased the aromatic selectivity for smaller aromatics such as benzene, toluene, and p-xylene and decreased the aromatic selectivity for bulkier ones such as m-xylene, o-xylene, and polyaromatics in CFP of beech wood relative to HSZM-5. In particular, the yield and selectivity of p-xylene, the most desired product from CFP of biomass, increased considerably from 1.64 C% and 33.3% for conventional HZSM-5 to 2.98–3.34 C% and 72.1–79.6% for the synthesized Ga-MFI zeolites. These results suggest that slightly reducing the pore size of MFI zeolite by Ga incorporation has a beneficial effect on optimizing the aromatic selectivity toward more valuable monoaromatic products, especially p-xylene, during CFP of biomass.

The metathesis of 2-butene (Trans and Cis) to propene was investigated over W-based catalysts. Thermodynamic calculations for metathesis and isomerization were carried out at various temperatures to test the reactions. The results showed that the WO₃/MCM-48 catalyst had good catalytic activity. The metathesis activity depended on the acidity of the catalyst and the dispersity of the WO₃ on the supports. High temperatures promoted the isomerization of 2-butene to 1-butene. According to thermodynamic analysis, however, this is adverse to the metathesis reaction, making it important to determine an appropriate reaction temperature.