Wire arc additive manufacturing (WAAM) has been considered as a promising technology for the production of large metallic structures with high deposition rates and low cost. Stainless steels are widely applied due to good mechanical properties and excellent corrosion resistance. This paper reviews the current status of stainless steel WAAM, covering the microstructure, mechanical properties, and defects related to different stainless steels and process parameters. Residual stress and distortion of the WAAM manufactured components are discussed. Specific WAAM techniques, material compositions, process parameters, shielding gas composition, post heat treatments, microstructure, and defects can significantly influence the mechanical properties of WAAM stainless steels. To achieve high quality WAAM stainless steel parts, there is still a strong need to further study the underlying physical metallurgy mechanisms of the WAAM process and post heat treatments to optimize the WAAM and heat treatment parameters and thus control the microstructure. WAAM samples often show considerable anisotropy both in microstructure and mechanical properties. The new in-situ rolling + WAAM process is very effective in reducing the anisotropy, which also can reduce the residual stress and distortion. For future industrial applications, fatigue properties, and corrosion behaviors of WAAMed stainless steels need to be deeply studied in the future. Additionally, further efforts should be made to improve the WAAM process to achieve faster deposition rates and better-quality control.

The Inconel 625 (IN625) superalloy has a high strength, excellent fatigue, and creep resistance under high-temperature and high-pressure conditions, and is one of the critical materials used for manufacturing high-temperature bearing parts of aeroengines. However, the poor workability of IN625 alloy prevents IN625 superalloy to be used in wider applications, especially in applications requiring high geometrical complexity. Laser powder bed fusion (LPBF) is a powerful additive manufacturing process which can produce metal parts with high geometrical complexity and freedom. This paper reviews the studies that have been done on LPBF of IN625 focusing on the microstructure, mechanical properties, the development of residual stresses, and the mechanism of defect formation. Mechanical properties such as microhardness, tensile properties, and fatigue properties reported by different researchers are systematically summarized and analyzed. Finally, the remaining issues and suggestions on future research on LPBF of IN625 alloy parts are put forward.

WC-Co hardmetals are widely used in wear-resistant parts, cutting tools, molds, and mining parts, owing to the combination of high hardness and high toughness. WC-Co hardmetal parts are usually produced by casting and powder metallurgy, which cannot manufacture parts with complex geometries and often require post-processing such as machining. Additive manufacturing (AM) technologies are able to fabricate parts with high geometric complexity and reduce post-processing. Therefore, additive manufacturing of WC-Co hardmetals has been widely studied in recent years. In this article, the current status of additive manufacturing of WC-Co hardmetals is reviewed. The advantages and disadvantages of different AM processes used for producing WC-Co parts, including selective laser melting (SLM), selective electron beam melting (SEBM), binder jet additive manufacturing (BJAM), 3D gel-printing (3DGP), and fused filament fabrication (FFF) are discussed. The studies on microstructures, defects, and mechanical properties of WC-Co parts manufactured by different AM processes are reviewed. Finally, the remaining challenges in additive manufacturing of WC-Co hardmetals are pointed out and suggestions on future research are discussed.

Martensitic stainless steels are widely used in industries due to their high strength and good corrosion resistance performance. Precipitation-hardened (PH) martensitic stainless steels feature very high strength compared with other stainless steels, around 3-4 times the strength of austenitic stainless steels such as 304 and 316. However, the poor workability due to the high strength and hardness induced by precipitation hardening limits the extensive utilization of PH stainless steels as structural components of complex shapes. Laser powder bed fusion (L-PBF) is an attractive additive manufacturing technology, which not only exhibits the advantages of producing complex and precise parts with a short lead time, but also avoids or reduces the subsequent machining process. In this review, the microstructures of martensitic stainless steels in the as-built state, as well as the effects of process parameters, building atmosphere, and heat treatments on the microstructures, are reviewed. Then, the characteristics of defects in the as-built state and the causes are specifically analyzed. Afterward, the effect of process parameters and heat treatment conditions on mechanical properties are summarized and reviewed. Finally, the remaining issues and suggestions on future research on L-PBF of martensitic precipitation-hardened stainless steels are put forward.

Aluminum alloy AA6111 and TiAl6V4 dissimilar alloys were successfully welded by high power ultrasonic spot welding. No visible intermetallic reaction layer was detected in as-welded AA6111/TiAl6V4 welds, even when transmission electron microscopy was used. The effects of welding time and natural aging on peak load and fracture energy were investigated. The peak load and fracture energy of welds increased with an increase in welding time and then reached a plateau. The lap shear strength (peak load) can reach the same level as that of similar Al–Al joints. After natural aging, the fracture mode of welds transferred from ductile fracture of the softened aluminum to interfacial failure due to the strength recovery of AA6111.