In order to obtain better cutting tool performance, the coatings appear as an alternative in the machining process. The goal of the coating is to improve tribological conditions in the chip-tool and tool-workpiece interfaces. On the other hand, the use of coated tools decreases the wear of the tools. This study discusses the ceramic coatings characterization deposited in WC tools. The Al₂O₃ and TiO₂ films present properties such as thermal stability, chemical inertia, high hardness, and good mechanical properties. These coatings were prepared by sol-gel technology. The results indicated that the multilayer coating presents better adhesion on the substrate. Moreover, lower coefficients of friction were found for the coated tools. The analysis of variance (ANOVA) was used to evaluate the influence of the cutting parameters and tool coating on the cutting force. The lower cutting force was obtained using the multilayer-coated tool. Thus, the sol-gel method appears as a novel technique to deposit coating in the WC tools to improve their performance.

This article aims to investigate the influence of different contact conditions on the friction properties of an Nb-stabilized AISI 430 ferritic stainless-steel sheet with deep drawing quality. Three tribological tests were performed: pin-on-disk, bending under tension, and strip-tension test. Moreover, counter samples of a hard metal (WC-12%Co) with surface finishes of 0.27 and 0.54 μm were used in the friction tests under dry and lubricated conditions. The influence of the texture and relative elongation of the strip on formability also were investigated. A comparative analysis of the results revealed that the coefficients of friction, wear, lubricant efficiency, and hardness measured below the wear surface indicated a strong dependence on surface roughness and the friction test type. The coefficients of friction obtained from the pin-on-disk test were higher than those obtained from the formability tests. In addition, the coefficient of friction increased with increasing relative elongation during the formability tests; it was higher in the bending-under-tension test than in the strip-tension test, mainly owing to the increasing strip surface roughness. The contact pressure during the formability tests was non-uniform during strip sliding under the tool. According to our results, for each friction condition in a specific area of the forming die, there is a value of the coefficient of friction, depending on the kinematic conditions. Therefore, the results can be used as input data to define design guidelines, improve productivity, and improve product quality from this steel sheet.