The key goal of this study was to characterize surface properties of chosen dental materials on the base on the contact angle measurements and surface free energy calculations. Tested materials were incubated in the simulated oral environment and drinks to estimate an influence of conditions similar to those in the oral cavity on wetting and energetic state of the surface. Types of materials were as follows: denture acrylic resins, composite and PET-G dental retainer to compare basic materials used in a prosthetics, restorative dentistry and orthodontics. The sessile drop method was used to measure the contact angle with the use of several liquids. Values of the surface free energies were estimated based on the Owens–Wendt, van Oss–Chaudhury–Good and Zisman’s methods. The research showed that surface wetting depends on the material composition and storage conditions. The most significance changes of CA were observed for acrylic resins (84.7° ± 3.8° to 65.5° ± 3.5°) and composites (58.8° ± 4.1° to 49.1° ± 5.7°) stored in orange juice, and for retainers (81.9° ± 1.8° to 99.6° ± 4.5°) incubated in the saline solution. An analysis of the critical surface energy showed that acrylic materials are in the zone of good adhesion (values above 40 mJ/m²), while BIS-GMA composites are in the zone of poor adhesion (values below 30 mJ/m²). Study of the surface energy of different dental materials may contribute to the development of the thermodynamic model of bacterial adhesion, based on the surface free energies, and accelerate the investigation of biomaterial interaction in the biological environment.

This article examines the impact of fatigue cycles on polylactide samples produced by 3D printing using the FDM method. Samples were printed in three infill degree variants: 50%, 75% and 100%. To compere the influence of infill degree on PLA properties, several tests, including the uniaxial tensile test, the low-cycle fatigue test, differential scanning calorimetry (DSC) and scanning electron microscopy (SEM), were conducted. Poisson’s ratio has also been studied. Single hysteresis loops were summed to obtain the entire low-fatigue cycle. The infill of density influenced all compared mechanical parameters. The decrease in infill degree caused the reduction of Young’s modulus and shear modulus. For a 100% degree of sample infill, a higher number of transferred load cycles were observed compared to PLA with 75% and 50% of infill. Additionally, the value of the transferred cyclic load before fatigue failure and the dissipation of mechanical energy was the highest for 100% of infill. It is also worth noting that fatigue tests can positively affect the appearance of the PLA structure. Obviously, it depends on the number of load cycles and the infill density. It causes that if the goal is to transfer as much load as possible over a long period of time, the maximum filling of the printed element should be used.

The key goal of this study was to characterize polytetrafluoroethylene (PTFE) based composites with the addition of bronze particles and mineral fibers/particles. The addition of individual fillers was as follows: bronze—30–60 wt.%, glass fibers—15–25 wt.%, coke flakes—25 wt.% and graphite particles—5 wt.%. Both static and dynamic tests were performed and the obtained results were compared with the microscopic structure of the obtained fractures. The research showed that the addition of 60 wt.% bronze and other mineral fillers improved the values obtained in the static compression test and in the case of composites with 25 wt.% glass fibers the increase was about 60%. Fatigue tests have been performed for the compression-compression load up to 100,000 cycles. All tested composites show a significant increase in the modulus as compared to the values obtained in the static compression test. The highest increase in the modulus in the dynamic test was obtained for composites with 25 wt.% of glass fibers (increase by 85%) and 25 wt.% of coke flakes (increase by 77%), while the lowest result was obtained for the lowest content of bronze particles (decrease by 8%). Dynamic tests have shown that composites with “semi-spherical” particles are characterized by the longest service life and a slower fatigue crack propagation rate than in the case of the long glass fibers. In addition, studies have shown that particles with smaller sizes and more spherical shape have a higher ability to dissipate mechanical energy, which allows their use in friction nodes. On the other hand, composites with glass fiber and graphite particles can be successfully used in applications requiring high stiffness with low amplitude vibrations.

The objective of the study was to analyze and compare fatigue properties of composites based on two biodegradable polymers: thermoplastic starch and polylactide blend filled with 10 wt% short flax fibers. Accelerated fatigue tests with increasing amplitude were done on neat polymers and their composites. Dissipated energy, strain and the temperature on the sample surface were the three characteristic values measured or calculated during the tests to evaluate fatigue stress of the materials with the use of Lehr’s method. The increase in temperature was not observed. Addition of flax fibers resulted in improvement of fatigue strength of polylactide-based composite but thermoplastic starch filled with flax fibers showed lower fatigue strength than neat polymer, shortened fatigue life and higher susceptibility to cyclic creep.