In this work, synthesis and investigations on chitosan-based hydrogels modified with Aloe vera juice are presented. These materials were synthesized by UV radiation. Investigations involved analysis of chemical structure by FTIR spectroscopy, sorption properties in physiological liquids, strength properties by texture analyzer, surface topography by Atomic Force Microscopy (AFM technique), and in vitro cytotoxicity by MTT test using L929 murine fibroblasts. Particular attention was focused both on determining the impact of the amount and the molecular weight of the crosslinker used for the synthesis as well as on the introduced additive on the properties of hydrogels. It was proven that modified hydrogels exhibited higher swelling ability. Introduced additive affected the tensile strength of hydrogels—modified materials showed 23% higher elongation. The greater amount of the crosslinker used in the synthesis, the more compact the structure, leading to the lower elasticity and lower sorption of hydrogels was reported. Above 95%, murine fibroblasts remained viable after 24 h incubation with hydrogels. It indicates that tested materials did not exhibit cytotoxicity toward these lines. Additionally, materials with Aloe vera juice were characterized by lower surface roughness. Conducted investigations allowed us to state that such modified hydrogels may be considered as useful for biomedical purposes.

In the study, polylactide-based (PLA) composites modified with natural particles (wood, bamboo, and cork) and with different levels of infilling (100%, 80%, and 60%) obtained by fused deposition modeling were tested. The effect of fiber type, infill level and crystallization rate on the mechanical properties were investigated by using tensile, flexural, and impact tests. The materials were subjected to mechanical tests carried out at 23 and 80 °C. Differential scanning calorimetry were employed to analyze crystallization behavior of composite. Furthermore, hydrothermal degradation was performed, and its effect on the properties was analyzed. The addition of natural fillers and different levels of infilling result in a similar level of reduction in the properties. However, the addition of natural fillers resulted in a slightly lower drop than the lowered infilling rate − 40% and 50% for tensile strength, respectively. Moreover, it was found that, composites made of PLA are more sensitive to high temperatures than to water. The decrease in Young's modulus of PLA at 80 °C was 90%, while after 28 days of hydrodegradation ~ 9%. The addition of fibers reduced this decrease at elevated temperatures. Importantly, in the case of a brittle material such as PLA, the impact strength has been improved by 50% for composites with cork particles and other lignocellulosic composites remained at the same level as for resin. Generally, the thermal treatment of composites increased the degree of crystallinity of the materials, as reflected in the higher results of mechanical tests.

The study evaluated the possibility of using natural fibers as a reinforcement of bio-polyethylene. Flax, coconut, basalt fiber, and wood flour were used in the work. Strength tests like static tensile test, three-point flexural test, or impact strength showed a positive effect of reinforcing bio-polyethylene-based composites. The effect of water and thermal ageing on the mechanical behavior of composites was assessed. In order to analyze the structure, SEM microscope images were taken and the effect of natural fibers on the change in the nature of cracking of composites was presented. Composites with natural fibers at a content of 12% by weight, resulting in increase of strength and rigidity of materials. The greatest strengthening effect for natural fibers was obtained for the composite with basalt fibers.

This paper discusses the possibility of using the process of geopolymerization to immobilize ash from municipal waste incineration plants. Fly ash used in the related research came from the same incineration plant, one of the biggest in Poland. The examination was conducted on the waste samples labeled as 190107* and 190113*. The comparison included such properties of waste as chemical composition, dioxin content, and size and morphology of particles. The waste was solidified in geopolymer matrix made from (i) fly ash from the combustion of bituminous coal or (ii) metakaolin. The waste percentages were 50 mass% and 70 mass%, respectively. Moreover, leaching tests were carried out and mechanical properties of the geopolymers materials containing immobilized ashes were analyzed. It was proved that geopolymerization process allows for the high-level immobilization of compounds and elements such as chlorides, sulfates, fluorides, barium, and zinc. Additionally, it was observed that in the case of the geopolymer samples containing 70 mass% of 190107* waste, the average compressive strength exceeded 18 MPa. Implications: A novel aspect of the results presented in this paper is the comprehensive investigation of the immobilization of large amounts of hazardous waste by means of the synthesis of geopolymers from metakaolin or coal fly ash. According to these results, it was determined that the level of immobilization is much higher in the case of the geopolymers based on metakaolin in comparison with geopolymers made from coal fly ash. On the basis on the obtained results, investigated geopolymers may be successfully used, e.g., as barriers or linear drains in landfills.

This article examines the impact of fatigue cycles on polylactide samples produced by 3D printing using the FDM method. Samples were printed in three infill degree variants: 50%, 75% and 100%. To compere the influence of infill degree on PLA properties, several tests, including the uniaxial tensile test, the low-cycle fatigue test, differential scanning calorimetry (DSC) and scanning electron microscopy (SEM), were conducted. Poisson’s ratio has also been studied. Single hysteresis loops were summed to obtain the entire low-fatigue cycle. The infill of density influenced all compared mechanical parameters. The decrease in infill degree caused the reduction of Young’s modulus and shear modulus. For a 100% degree of sample infill, a higher number of transferred load cycles were observed compared to PLA with 75% and 50% of infill. Additionally, the value of the transferred cyclic load before fatigue failure and the dissipation of mechanical energy was the highest for 100% of infill. It is also worth noting that fatigue tests can positively affect the appearance of the PLA structure. Obviously, it depends on the number of load cycles and the infill density. It causes that if the goal is to transfer as much load as possible over a long period of time, the maximum filling of the printed element should be used.

This study showed that several mechanisms of the basal resistance of winter triticale to M icrodochium nivale are cultivar‐dependent and can be induced specifically during plant hardening. Experiments and microscopic observations were conducted on triticale cvs H ewo (able to develop resistance after cold treatment) and M agnat (susceptible to infection despite hardening). In cv. H ewo, cold hardening altered the physical and chemical properties of the leaf surface and prevented both adhesion of M . nivale hyphae to the leaves and direct penetration of the epidermis. Cold‐induced submicron‐ and micron‐scale roughness on the leaf epidermis resulted in superhydrophobicity, restricting fungal adhesion and growth, while the lower permeability and altered chemical composition of the host cell wall protected against tissue digestion by the fungus. The fungal strategy to access the nutrient resources of resistant hosts is the penetration of leaf tissues through stomata, followed by biotrophic intercellular growth of individual hyphae and the formation of haustoria‐like structures within mesophyll cells. In contrast, a destructive necrotrophic fungal lifestyle occurs in susceptible seedlings, despite cold hardening of the plants, with the host epidermis, mesophyll and vascular tissues being digested and becoming disorganized as a result of the low chemical and mechanical stability of the cell wall matrix. This work indicates that specific genetically encoded physical and mechanical properties of the cell wall and leaf tissues that depend on cold hardening are factors that can determine plant resistance against fungal diseases.