With the progress of science and technology, intelligent wearable devices have become more and more popular in our daily life. Hydrogels are widely used in flexible sensors due to their good tensile and electrical conductivity. However, traditional water-based hydrogels are limited by shortcomings of water retention and frost resistance if they are used as the application materials of flexible sensors. In this study, the composite hydrogels formed by polyacrylamide (PAM) and TEMPO-Oxidized Cellulose Nanofibers (TOCNs) are immersed in LiCl/CaCl₂/GI solvent to form double network (DN) hydrogel with better mechanical properties. The method of solvent replacement give the hydrogel good water retention and frost resistance, and the weight retention rate of the hydrogel was 80.5% after 15 days. The organic hydrogels still have good electrical and mechanical properties after 10 months, and can work normally at −20 °C, and has excellent transparency. The organic hydrogel show satisfactory sensitivity to tensile deformation, which has great potential in the field of strain sensors.

Cellulose detectors, as green sensors, are some of the defensive mechanisms of plants which combat environmental stresses. However, extracted cellulose struggles to fulfil these functionalities due to its rigid physical/chemical properties. In this study, a novel cellulose dual-crosslinked framework (CDCF) is proposed. This comprises a denser temporary physical crosslinking bond (hydrogen bonding) and a looser covalent crosslinking bond (N,N-methylenebisacrylamide), which create deformable spaces between the two crosslinking sites. Abundant pH-sensitive carboxyl groups and ultralight, highly porous structures make CDCF response very sensitive in acid/alkaline vapor environments. Hence, a significant shrinkage of CDCF was observed following exposure to vapors. Moreover, a curcumin-incorporated CDCF exhibited dual shape and color changes when exposed to acid/alkaline vapors, demonstrating great potential for the multi-detection of acid/alkaline vapors.