The development of magnetic field sensors for biomedical applications primarily focuses on equivalent magnetic noise reduction or overall design improvement in order to make them smaller and cheaper while keeping the required values of a limit of detection. One of the cutting-edge topics today is the use of magnetic field sensors for applications such as magnetocardiography, magnetotomography, magnetomyography, magnetoneurography, or their application in point-of-care devices. This introductory review focuses on modern magnetic field sensors suitable for biomedicine applications from a physical point of view and provides an overview of recent studies in this field. Types of magnetic field sensors include direct current superconducting quantum interference devices, search coil, fluxgate, magnetoelectric, giant magneto-impedance, anisotropic/giant/tunneling magnetoresistance, optically pumped, cavity optomechanical, Hall effect, magnetoelastic, spin wave interferometry, and those based on the behavior of nitrogen-vacancy centers in the atomic lattice of diamond.

Polymer-based magnetoelectric composite materials have attracted a lot of attention due to their high potential in various types of applications as magnetic field sensors, energy harvesting, and biomedical devices. Current researches are focused on the increase in the efficiency of magnetoelectric transformation. In this work, a new strategy of arrangement of clusters of magnetic nanoparticles by an external magnetic field in PVDF and PFVD-TrFE matrixes is proposed to increase the voltage coefficient (α_ME) of the magnetoelectric effect. Another strategy is the use of 3-component composites through the inclusion of piezoelectric BaTiO₃ particles. Developed strategies allow us to increase the α_ME value from ~5 mV/cm·Oe for the composite of randomly distributed CoFe₂O₄ nanoparticles in PVDF matrix to ~18.5 mV/cm·Oe for a composite of magnetic particles in PVDF-TrFE matrix with 5%wt of piezoelectric particles. The applicability of such materials as bioactive surface is demonstrated on neural crest stem cell cultures.

Three-dimensional printing is one of the most promising areas of additive manufacturing with a constantly growing range of applications. One of the current tasks is the development of new functional materials that would allow the manufacture of objects with defined magnetic, electrical, and other properties. In this work, composite magnetic filaments for 3D printing with tunable magnetic properties were produced from polylactic acid thermoplastic polymer with the addition of magnetic ferrite particles of different size and chemical composition. The used magnetic particles were cobalt ferrite CoFe₂O₄ nanoparticles, a mixture of CoFe₂O₄ and zinc-substituted cobalt ferrite Zn_0.3Co_0.7Fe₂O₄ nanoparticles (~20 nm), and barium hexaferrite BaFe₁₂O₁₉ microparticles (<40 µm). The maximum coercivity field H_C = 1.6 ± 0.1 kOe was found for the filament sample with the inclusion of 5 wt.% barium hexaferrite microparticles, and the minimum H_C was for a filament with a mixture of cobalt and zinc–cobalt spinel ferrites. Capabilities of the FDM 3D printing method to produce parts having simple (ring) and complex geometric shapes (honeycomb structures) with the magnetic composite filament were demonstrated.

This research is devoted to the fabrication of 5-nm thick permalloy film-based magnetoplasmonic crystal for magnetic field sensing applications. Optical and magneto-optical activity of the magnetoplasmonic crystal is studied with the means of numerical modeling and spectroscopy techniques. The studied sample achieves sensitivity to an external DC magnetic field of 7.5 mOe in the 5.1 Oe required modulation AC magnetic field. Obtained experimental and modeling results can be used for the fabrication of cheaper and more energy-efficient sensing elements for magnetoplasmonic crystal-based magnetic field sensors due to the reduction of required ferromagnetic material and modulation magnetic field.

The combination of plasmonic material and magnetic metal oxide nanoparticles is widely used in multifunctional nanosystems. Here we propose a method for the fabrication of a gold/cobalt ferrite nanocomposite for biomedical applications. The composite includes gold cores of ~10 nm in diameter coated with arginine, which are surrounded by small cobalt ferrite nanoparticles with diameters of ~5 nm covered with dihydrocaffeic acid. The structure and elemental composition, morphology and dimensions, magnetic and optical properties, and biocompatibility of new nanocomposite were studied. The magnetic properties of the composite are mostly determined by the superparamagnetic state of cobalt ferrite nanoparticles, and optical properties are influenced by the localized plasmon resonance in gold nanoparticles. The cytotoxicity of gold/cobalt ferrite nanocomposite was tested using T-lymphoblastic leukemia and peripheral blood mononuclear cells. Studied composite has selective citotoxic effect on cancerous cells while it has no cytotoxic effect on healtly cells. The results suggest that this material can be explored in the future for combined photothermal treatment and magnetic theranostic.