In an effort to support the large-scale implementation of clean hydrogen in industry and society, the electrolytic decomposition of water is considered a realistically enticing prospect, provided the guarantee of affordable and durable material components. Within alkaline systems, earth-abundant electrocatalysts could provide both these requirements. However, a continued exploration of the reactivity and the causes behind different behaviors in performance are necessary to guide optimization and design. In this paper, Ta-doped NiO thin films are prepared via DC magnetron sputtering (1-2-4 at % Ta) to demonstrate the effect of surface electronic modulation by non-3d elements on the catalysis of the oxygen evolution reaction (OER). Material properties of the catalysts are analyzed via Rutherford backscattering spectrometry, X-ray diffractometry, photoelectron spectroscopy, and Raman spectroscopy. Ta impurities are shown to be directly responsible for increasing the valence state of Ni sites and enhancing reaction kinetics, resulting in performance improvements of up to 64 mV at 10 mA cm^-2 relative to pristine NiO. Particularly, we show that by applying operando Raman spectroscopy, Ta enhances the ability to create high-valence Ni in γ-NiOOH at a lower overpotential compared to the undoped sample. The lowered overpotentials of the OER can thus be attributed to the energetically less hindered advent of the creation of γ-NiOOH species on the pre-catalyst surface: a phenomenon otherwise unresolved through simple voltammetry.

Direct solar hydrogen generation via a combination of photovoltaics (PV) and water electrolysis can potentially ensure a sustainable energy supply while minimizing greenhouse emissions. The PECSYS project aims at demonstrating a solar‐driven electrochemical hydrogen generation system with an area >10 m²with high efficiency and at reasonable cost. Thermally integrated PV electrolyzers (ECs) using thin‐film silicon, undoped, and silver‐doped Cu(In,Ga)Se₂and silicon heterojunction PV combined with alkaline electrolysis to form one unit are developed on a prototype level with solar collection areas in the range from 64 to 2600 cm²with the solar‐to‐hydrogen (StH) efficiency ranging from ≈4 to 13%. Electrical direct coupling of PV modules to a proton exchange membrane EC to test the effects of bifaciality (730 cm²solar collection area) and to study the long‐term operation under outdoor conditions (10 m²collection area) is also investigated. In both cases, StH efficiencies exceeding 10% can be maintained over the test periods used. All the StH efficiencies reported are based on measured gas outflow using mass flow meters.

In this work, a trimetallic NiMoV catalyst is developed for the hydrogen evolution reaction and characterized with respect to structure, valence, and elemental distribution. The overpotential to drive a 10 mA cm−2 current density is lowered from 94 to 78 mV versus reversible hydrogen electrode by introducing V into NiMo. A scalable stand-alone system for solar-driven water splitting was examined for a laboratory-scale device with 1.6 cm2 photovoltaic (PV) module area to an up-scaled device with 100 cm2 area. The NiMoV cathodic catalyst is combined with a NiO anode in alkaline electrolyzer unit thermally connected to synthesized (Ag,Cu) (In,Ga)Se2 ((A)CIGS) PV modules. Performance of 3- and 4-cell interconnected PV modules, electrolyzer, and hydrogen production of the PV electrolyzer are examined between 25°C and 50°C. The PV-electrolysis device having a 4-cell (A)CIGS under 100 mW cm−2 illumination and NiMoV-NiO electrolyzer shows 9.1% maximum and 8.5% averaged efficiency for 100 h operation.